PC/SC-1100R homopolymer for injection moulding applications with High transparency and high gloss
The product is used for optic lighting, electronic appliances, mechanical equipment
Optic lighting: Used in the manufacture of large chimney, protective glass Also can be used in transparent material on the plane.
Electronic appliances such as CD, telephones, computers, videos and so on
Mechanical equipment: Used in the manufacture of all kinds of parts Also can be used to make machine shell and frame.
Others: Can be used for toys, model and so on
| Project |
Test conditions [state] |
Test method |
Test data |
Data unit |
| Density |
|
AS TM D792 |
1.20 |
G/cm3 |
| Water absorpotion |
|
ASTM D570 |
0.20 |
% |
| MFR |
300ºC 1.2kg |
ASTM D1238 |
10 |
g/10min |
| vicat softening temperature |
|
ASTM D1525 |
150 |
ºC |
| tensile strength |
|
ASTM D638 |
630 |
kgf/cm2 |
| bending strength |
2.8mm/min |
ASTM D790 |
920 |
kgf/cm2 |
| flexural modulus |
2.8mm/min |
ASTM D790 |
24000 |
kgf/cm2 |
NIIS
|
1/8 |
ASTM D256 |
87 |
kgf/cm2 |
| Rockwell hardness |
|
ASTM D785 |
77 |
M |
distortion temperature
|
0.45Mpa |
ASTM D648 |
138 |
ºC |
distortion temperature
|
1.8Mpa |
ASTM D648 |
125 |
ºC |
molding shrinkage
|
|
ASTM D955 |
0.5-0.7 |
% |
| Project |
Test conditions [state] |
Test method |
Test data |
Data unit |
| Density |
|
AS TM D792 |
1.20 |
G/cm3 |
| Water absorpotion |
|
ASTM D570 |
0.20 |
% |
| MFR |
300ºC 1.2kg |
ASTM D1238 |
10 |
g/10min |
| vicat softening temperature |
|
ASTM D1525 |
150 |
ºC |
| tensile strength |
|
ASTM D638 |
630 |
kgf/cm2 |
| bending strength |
2.8mm/min |
ASTM D790 |
920 |
kgf/cm2 |
| flexural modulus |
2.8mm/min |
ASTM D790 |
24000 |
kgf/cm2 |
NIIS
|
1/8 |
ASTM D256 |
87 |
kgf/cm2 |
| Rockwell hardness |
|
ASTM D785 |
77 |
M |
distortion temperature
|
0.45Mpa |
ASTM D648 |
138 |
ºC |
distortion temperature
|
1.8Mpa |
ASTM D648 |
125 |
ºC |
molding shrinkage
|
|
ASTM D955 |
0.5-0.7 |
% |