The Best Price of LLDPE

• Customization: Available
• Material: Linear Low Density Polyethylene/LLDPE
• Usage: General Plastics
• Model NO.: 118W
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film/Injection/Blow/Extrusion
• Color: According to Your Demand
• Type: PE
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Grade: Injection Molding Grade
• Transport Package: 25kg/Bag
• Specification: international standard
• Origin: China
• HS Code: 3901200090
• Production Capacity: 200t/Month

Product Description

1.picture



2.TDS

Project	Test Condition	Test Data	Data Unit
MFI	ASTM D-1238	1.0	g/10min
Density	ASTM D-792	0.918	g/cm³
Yield tensile strength	ASTM D-882	11	Mpa
Tensile strength at break	ASTM D-882	32	Mpa
Elongation at break	ASTM D-882	750	%
Impact resistance		68	MJ/M²
Turbidity%	ASTM D-1003	9.5	%

Specification level
Film and other
Data sheet   

Project	Test Condition	Test Data	Data Unit
MFI	ASTM D-1238	1.0	g/10min
Density	ASTM D-792	0.918	g/cm³
Yield tensile strength	ASTM D-882	11	Mpa
Tensile strength at break	ASTM D-882	32	MPa
Elongation at break	ASTM D-882	750	%
Impact resistance		68	MJ/M²
Turbidity	ASTM D-1003	9.5	%

APPLICATIONS
General film

LLDPE 218W
 

Project	Test method	Test Data			Data Unit
MFR(190ºC,2.16ºC)		2			g/10min
Density		0.918			g/cm³
Yield tensile strength		MD	12		Mpa
		TD	10
Tensile strength at break		MD	35		MPa
		TD	29
Elongation at break		MD		700	%
		TD		750
Secant modulus		MD1%		220	Mpa
		TD1%		260
Haze		13			%
Elmandorf tear strength		MD		130	g
		TD		320
Vicat softening point		98			ºC
Glossiness		80

LLDPE 7042

Item	Test method	Test data	Data unit
Density	GB/T 1033	0.917-0.923	g/cm3
MFR	GB/T 3682	1.5-2.5	g/10min
Tensile yield strength	GB/T 1040	≥8.3	Mpa
Tensile breaking strength	GB/T 1040	≥12	Mpa
Elongation at break	GB/T 1040	≥500	%
Granular appearance	SH/T 1541	Large particles and small particles	≤10 g/kg
		Snakeskin and silk hair	≤40 apiece/kg
		pollution particles	≤40 apiece/kg
Fisheye, 0.4 mm		≤40	apiece/1520 c
Fisheye, 0.8 mm		≤8	apiece/1520 c