2022 Virgin/Recycled PP Granule for Making Container

• Customization: Available
• Material: Polypropylene/PP
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Model NO.: PP 8303
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film Pressure
• Color: White
• Application: for Extrusion
• Transport Package: 25kg/Bag
• Specification: COA
• Trademark: self produce
• Origin: China
• HS Code: 3901200090
• Production Capacity: 300

Product Description

Specification rankTransparent

Appearance colorWhite transparent color

Performance	Test conditions [state]	Test data	Data unit
Density		0.9	g/m3
Melt flow rate		10	g/10min
Tensile yield strength		25	Mpa
Elongation at break		≥600	%
Notch impact strength	23ºC	8	kj/m2
Flexural modulus		≥1000	Mpa
Rockwell hardness		90	R
Load heat distortion temperature		80	ºC

   
PP 66M10T

Data sheet      

Item		Test method	Test data	Data unit
Density		ASTM D-792	0.905	g/cm3
MFR		ASTM D-1238	3.5	g/10min
Tensile yield strength		ASTM D-638	23	Mpa
The yield tensile elongation		ASTM D-638	10	%
Rockwell hardness		ASTM D-785	80	%
notched izod impact strength	-20ºC	ASTM D-256	100	J
	23ºC	ASTM D-256	750	J/m
Flexural modulus		ASTM D-790A	1000	Mpa
HDT		ASTM D-648	85	ºC
Vicat Softening Temperature		ASTM D-1525B	145	ºC

Data sheet      

Item			Test method	Test data	Data unit
MFR			GB/T 3682-2000	3.19	g/10min
Mould Shrinkage	Parallel		GB/T 17037.4-2003	1.6	%
	Vertical		GB/T 17037.4-2003	1.7	%
Flexural Modulus			GB/T 9341-2000	1105	Mpa
Tensile yield stress			GB/T 1040.2-2006	23	Mpa
Charpy Notched Impact Strength		-20ºC	GB/T 1043-2008	8.4	KJ/m2
		23ºC	GB/T 1043-2008	20	KJ/m2
Rockwell hardness			GB/T 3398.2-2008	87
HDT			GB/T 1634.1-2004	76	ºC
Ash content			GB/T 9345.1-2008	0.011	%