Description
PA6 1013B is copolymerization for injection molding with the safety and reliability of the excellent stability.
Application
The product is used for making used in auto parts, power tools,electrical outlet, building materials.
| Total |
| Material's state |
?Current valid |
| Processing method |
?Injection molding |
| Appearance |
?White |
| Application |
?Auto parts,building materials |
| Physical property |
Rating |
Test method |
| Density |
1.14 g/cm3 |
| MFR(230ºC,2.16KG) |
15.49g/10min |
GB/T 3682-2000 |
| Mechanical property |
Rating |
Test method |
| Tensile strength |
59.21MPa |
GB/T 1040-1992 |
| Elongation at break |
123.67/v50% |
GB/T 1040-1992 |
| Flexural strength |
68.79 MPa |
GB/T 9341-2000 |
| Flexural modulus |
1.51GPa |
GB/T 9341-2000 |
| Impact property |
Rating |
Test method |
| Charpy Notched Impact Strength |
29.51KJ/m2 |
GB/T 1043-1993 |
| Charpy impact strength |
25JNBKJ/m2 |
GB/T 1043-1993 |
| Other property |
Rating |
Test method |
| Relative viscosity deviation |
<0.02WT% |
| Relative viscosity |
2.75 |
| Viscosity |
2.81 |
GB/T 1632-1993 |
| Water content |
0.06WT% |
| Tio2content |
0-1.3WT% |