| Material: | Polypropylene/PP |
|---|---|
| Usage: | General Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Film Pressure |
| Color: | Transparency |
| Mfr: | 40g/10min |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
| Total | ||
| Material's state | Current valid | |
| Performance feature | Rigidity and high polymer | |
| Application | Cosmetic packaging,thin-wall, food packaging | |
| Appearance | Clear/transparency | |
| Processing method | Injection molding | |
physical property |
Rating |
Test method |
| Proportion | 0.905g/cm³ | ASTM D792 |
| MFR(230ºC/2.16kg) | 40g/10min | ASTM D1238 |
| Mechanical property | Rating | Test method |
| Tensile strength(yield) | 36.0 Mpa | ASTM D638 |
| Elongation(yield) | 11% | ASTM D638 |
| Flexural modulus | 1500Mpa | ASTM D790 |
| Impact property | Rating | Test method |
| Notched IZOD impact strength(23ºC) | 20J/m | ASTM D256 |
| Hardness | Rating | Test method |
| Rockwell hardness® | 103 | ASTM D785 |
| Thermal property | Rating | Test method |
| Distortion temperature | ASTM D648 | |
| 0.45Mpa | 113ºC | |
| 1.8Mpa | 59.0ºC | |
| Vicat softening point | 153ºC | ASTM D1525 |
| Optical property | Rating | Test method |
| Haze | 18% | ASTM D1003 |