| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 3901200090 |
| Material: | High Density Polyethylene/HDPE |
| Usage: | General Plastics, Blowing Moulding |
| Plastic Properties After Heated: | Thermosetting Plastic |
| Plastic Forming Method: | Blow Molding |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
Item |
Test condition |
Test Method |
Value |
Unit |
Density |
ISO 1183 |
0.944-0.955 |
g/cm3 |
|
MFR |
190°C/2.16kg |
ISO 1133 |
0.03-0.07 |
g/10min |
Tensile strength at yield |
ISO 527-2 |
22 |
MPa |
|
Elongation at break |
ISO 527-2 |
>350 |
% |
|
ESCR |
F50,50°C,100% |
ASTM D-1693A |
1000 |
h |
VICAT |
ASTM D-1525 |
126 |
°C |
Item |
Test Condition |
Test Method |
Value |
Unit |
Density |
ISO 1183 |
0.950~0.955 |
g/cm |
|
MFR |
190°C/2.16kg |
ISO 1133 |
1.7~2.5 |
g/10min |
Tensile strength at yield |
ISO 527-2 |
24 |
MPa |
|
Elongation at break |
ISO 527-2 |
>600 |
% |
Item |
Test Condition |
Test Method |
Value |
Unit |
MFR |
190°C/2.16kg |
ASTM D-1238 |
20 |
g/10min |
Density |
--- |
ASTM D-792 |
0.954 |
g/cm3 |
Tensile strength at yiled |
--- |
ASTM D-638 |
28 |
MPa |
Elongation at break |
--- |
ASTM D-638 |
250 |
% |
Impact tensile strength |
--- |
ASTM D-1822 |
42 |
kJ/m2 |
ESCR |
ASTM D-1693 |
3 |
--- |
|
VACIT |
--- |
ASTM D-1525 |
127 |
°C |