PA6 1013B is copolymerization for injection molding with the safety
and reliability of the excellent stability.
PA6 has high tensile strength, resistance and tough, impact resistant, self-lubricating, wear resistance, chemical resistance, low temperature resistance, etc.
Description: Copolymerization; Injection molding; The excellent stability.
Application: Auto parts, power tools, electrical outlet, building materials.
The product is used for making used in auto parts, power tools,
electrical outlet, building materials.
Material's state: Current valid
Total |
Material's state |
?Current valid |
Processing method |
?Injection molding |
Appearance |
?White |
Application |
?Auto parts,building materials |
Physical property |
Rating |
Test method |
Density |
1.14 g/cm3 |
MFR(230ºC,2.16KG) |
15.49g/10min |
GB/T 3682-2000 |
Mechanical property |
Rating |
Test method |
Tensile strength |
59.21MPa |
GB/T 1040-1992 |
Elongation at break |
123.67/v50% |
GB/T 1040-1992 |
Flexural strength |
68.79 MPa |
GB/T 9341-2000 |
Flexural modulus |
1.51GPa |
GB/T 9341-2000 |
Impact property |
Rating |
Test method |
Charpy Notched Impact Strength |
29.51KJ/m2 |
GB/T 1043-1993 |
Charpy impact strength |
25JNBKJ/m2 |
GB/T 1043-1993 |
Other property |
Rating |
Test method |
Relative viscosity deviation |
<0.02WT% |
Relative viscosity |
2.75 |
Viscosity |
2.81 |
GB/T 1632-1993 |
Water content |
0.06WT% |
Tio2content |
0-1.3WT% |
NOTE ISO 9001 2000 |
If you need the product ,hope you could contact me anytime, I will offer the detailed information and the competitive price fopr your reference.