LDPE 2102TX00 is for film moulding applications.
Used for making bags
Packing: 25kg/bag
Delivery time: Within 15days after receive the advanced payment
Payment terms: 30%T/T in advance, the balance70%should be paid agaist the copy of B/L
| Impulse strength |
20kJ/m |
ASTM D-4272 |
| Tearing strength(MD) |
70kN/m |
ISO 6383-2 |
| Tearing strength(TD) |
25kN/m |
ISO 6383-2 |
| Yield stress(MD) |
11MPa |
ISO 527-3 |
| Yield stress(TD) |
11MPa |
ISO 527-3 |
| Rupture stress(MD) |
30MPa |
ISO 527-3 |
| Rupture stress(TD) |
7MPa |
ISO 527-3 |
| Elongation at break(MD) |
>100% |
ISO 527-3 |
| Elongation at break(TD) |
>500% |
ISO 527-3 |
| Elasticity modulus(MD) |
190MPa |
ISO 527-3 |
| Elasticity modulus(TD) |
190MPa |
ISO 527-3 |
| Frictional coefficient |
>1 |
ASTM D-1894 |
| Optical property |
Rating |
Test method |
| Glossiness |
53% |
ASTM D-2457 |
| Haze |
10% |
ASTM D-1003A |
| Transparency |
26% |
SABIC method |
| |
NOTE |
ISO 9001 2000 |
Audited Supplier 