Material: | Low Density Polyethylene/LDPE |
---|---|
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Film/Blow/Injection/Extrusion |
Color: | White |
Delivery: | Within 10 Days After Receiving Deposit |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Impulse strength | 20kJ/m | ASTM D-4272 |
Tearing strength(MD) | 70kN/m | ISO 6383-2 |
Tearing strength(TD) | 25kN/m | ISO 6383-2 |
Yield stress(MD) | 11MPa | ISO 527-3 |
Yield stress(TD) | 11MPa | ISO 527-3 |
Rupture stress(MD) | 30MPa | ISO 527-3 |
Rupture stress(TD) | 7MPa | ISO 527-3 |
Elongation at break(MD) | >100% | ISO 527-3 |
Elongation at break(TD) | >500% | ISO 527-3 |
Elasticity modulus(MD) | 190MPa | ISO 527-3 |
Elasticity modulus(TD) | 190MPa | ISO 527-3 |
Frictional coefficient | >1 | ASTM D-1894 |
Optical property | Rating | Test method |
Glossiness | 53% | ASTM D-2457 |
Haze | 10% | ASTM D-1003A |
Transparency | 26% | SABIC method |
NOTE | ISO 9001 2000 |