| Performance | Test Method | Test data | Data unit |
| Melt flow rate | ISO 1133 | 3.0 | g/10min |
| Density | ISO 1183 | 1050 | kg/m3 |
| Water Absorption | ISO 62 | 0.1 | % |
| Tensile Modulus | ISO 527-2 | 3000 | Mpa |
| Tensile breaking strength | ISO 527-2 | 50.0 | Mpa |
| Tensile stain at break | ISO 527-2 | 2.0 | % |
| Tensile creep modulus | ISO 899-1 | 3150 | Mpa |
| Notched impact strength of simply supported beams | ISO 179/1eU | 16.0 | kJ/m² |
| Surface Resistivity | IEC 60093 | 1.0E+14 | ohms |
| Heat Deflection Temperature | ISO 75-2 | 97.0 | °C |
| Vicat softening point | ISO 306 | 98.0 | ºC |
| Item | Test condition | Test method | Test data | Data unit |
| MFR | 200°C,5kg | ISO 1133 | 8 | cm3/10min |
| Density | ISO 1183 | 1.04 | g/cm3 | |
| Tensile elongation at break | ISO 527 | 2 | % | |
| Bending strength | ISO 178 | 78 | MPa | |
| Vicat softing temperature | B/503,50N,50°C/h | ISO 306 | 88 | °C |
| Distortion temperature | 0.45MPa | ISO 75 | 86 | °C |
| Charpy notched impact strength | 23°C | ISO 179/1eA | 3 | KJ/m2 |
| Charpy impact strength | 23°C | ISO179/1eU | 17 | KJ/m2 |
| IZOD impact strength | 23°C | ISO180 | 11 | KJ/m2 |
| Tensile yield stress | ISO527 | 47 | Mpa | |
| Tensile Modulus | ISO527 | 3300 | Mpa | |
| Rockwell hardness | ASTM D-785 | 100 | L |