Lightweight LDPE/Low-Density Polyethylene Film Grade

• Customization: Available
• Feature: Biodegradable
• CAS No.: 45496561230
• Model NO.: LDPE 100AC, 2100TN00, 2426H
• Formula: 45455120089
• EINECS: 15482030212
• Material: Low Density Polyethylene/LDPE
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film/Blow/Injection/Extrution
• Color: Transparent
• Type: Virgin/Recycled LDPE
• Payment: T/T L/C
• Delivery: Within 15 Days After Receiving Deposit
• Processing Method: Film/Extrution/Blow/Injection
• Transport Package: 25kg/Bag
• Specification: international standard
• Trademark: Self-produced
• Origin: China
• HS Code: 3901902000
• Production Capacity: 500t/Month
• Package Size: 80.00cm * 55.00cm * 25.00cm
• Package Gross Weight: 25.000kg

Product Description

Product Description

LDPE 100AC

Specification level
Blow film grade
    

Project		Test data	Data unit
Basic properties	Density	0.9205~0.9245	g/cm3
	Melt flow rate	1.7-2.3	g/10min
Mechanical properties	Elongation at break	≥200	%
	Tensile strength at break	≥17	Mpa
	Tensile strength yield	≥3.0
	Shore hardness	≥44
Thermal properties	Vicat softening point	≥90	ºC

APPLICATIONS
Used for agricultural film, shrink film, transparent film, shopping bags, frozen bags, packaging bags

Description:
             LLDPE / linear low density polyethylene virgin and recycle granules 
               1.Free Sample 
               2.SGS/CIQ Test 
               3.Factory Price/Quality
Specifications:
 
 
Film Grade
 

Tests	Value	Unit
Melt Flow Rate (MFR)	2.0±0.4	g/10min
Density	920±2	Kg/cm3
Tensile Strengthat Yield	8	Mpa ≥
Tensile Strengthat Break	12	Mpa ≥
haze	15	%≤
Packing	In 25 kg PP woven bags,20MT/20'FCL

 
 Master Batch Use  
 
 

Tests	Value	Unit
Melt Flow Rate (MFR)	20	g/10min
Density	0.924	g/cm3
Tensile Strength	MD12	Mpa
	TD 10
Elongation at Yield	13	%
Elongation at Break	200
Dark Drop Impact	105	g
Brittle Temperature(F 50)	-70	°C
Vicat Softening Point	90	°C
Packing	In 25 kg wovenbags,20MT/20'FCL

 
 
Powder Rotational Molding Grade  
 
 

Tests	Value	Unit
Melt Flow Rate (MFR)	3.2	g/10min
Density	0.939	g/cm3
Melting Point	127	°C
Tensile Yield Strength	21	Mpa
Tensile Strength at Break	28	Mpa
Elongation at Break	1,100	%
Flexural Modulus	750	Mpa
Brittle Temperature	<-60	°C

 
 
 Application:
                      Make barrela, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating.
LLDPE Specifications:

PROPERTY	UNIT	Data
Melt Flow Index	g/10min	≤1.0
Density	g/cm3	≤0.945
Tensile strength	Mpa	≥14.0
Elongation at break	%	≥600
Brittle temperature at low temperature	°C	≤-76
ESCR ,FO	H	≥500
Carbon Black dispersion	--	--
Tensile strength after thermal aging	Mpa	≥13
Elongation after thermal aging	%	≥500
Dielectric strength	Mv/m	≥25
Volume resistivity	Ω.m	≥1*1014
change rate of tensile strength  after weather aging environment of 0--1008h	%	±25
change rate of elongation  after weather aging environment of 0--1008h	%	±25
change rate of tensile strength  after weather aging environment of 504--1008h	%	±15
change rate of elongation after weather aging environment of 504--1008h	%	±15

 
LLDPE / linear low density polyethylene virgin and recycle granules 
               1.Free Sample 
               2.SGS/CIQ Test 
               3.Factory Price/Quality