Material: | Polypropylene/PP |
---|---|
Usage: | General Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Blow Molding |
Color: | According to Your Demand |
COA: | Plastic Materials |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Project performance | Test method | Test data | Data unit |
Density | 0.90 | g/cm3 | |
Melt flow rate | 20.0 | g/10min | |
HRC | 90 | R | |
Flexural Modulus | 12,500 | Kg/cm2 | |
Elongation | 20 | % | |
Tensile breaking strength | 290 | Kg/cm2 | |
Impact strength | 8(4) | Kg/cm2 | |
HDT | 110 | ºC | |
Vicat Softening Temperature | 150 | ºC |
Project performance | Test method | Test data | Data unit |
Density | 0.90 | g/cm3 | |
Melt flow rate | 20.0 | g/10min | |
HRC | 90 | R | |
Flexural Modulus | 12,500 | Kg/cm2 | |
Elongation | 20 | % | |
Tensile breaking strength | 290 | Kg/cm2 | |
Impact strength | 8(4) | Kg/cm2 | |
HDT | 110 | ºC | |
Vicat Softening Temperature | 150 | ºC |