Virgin ABS Acrylonitrile Butadiene Styrene Resin Granule Latest Price

• Material: Acrylonitrile-Butadiene-Styrene Copolymers/ABS
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Oyster White
• Appearance: Granule&Resin
• Model NO.: ABS h-050
• Name: ABS
• Transport Package: 25kg/PP Bag
• Specification: SGS
• Trademark: Sinopec
• Origin: China
• HS Code: 3904109090
• Production Capacity: 300t/Month

Product Description

Specification of ABS

Test Project	Test Methods	Unit	Typical Values [1]
Tensile Stress	GB/T1040-92	Mpa	28-40
Flexural Stress	GB/T 9341-2000	Mpa	48
Flexural Modulus	GB/T9341-2000	Mpa	≥1600
Notched Impact Strength	GB/T1043-93	KJ/m2	≥10
Elongation At Break	GB/T1040-92	%	40-80
Heat Distortion Temperature	GB/T1634-2004	°C	≥85
MFR	GB/T 3682-2000	g/10min	10-40
Flammability	GB/T 2408-1996	UL94	V-0
Testing Condition	23±2°C, 50±5%RH

The raw material description part
Specification level: Injection moulding grade
Color: White
Raw material technical data:
MFR(melt flow rate): 15.5 g/10min
Density: 1.045 g/cm3
Mechanical properties of tensile strength 1/8", 50mm/min ASTM D-638 510 kg/cm2
Stretch rate 1/8", 50mm/min ASTM D-638 40 %
Flexural strength 1/8", 1.3mm/min ASTM D-790 770 kg/cm2
Flexural modulus 1/8", 1.3mm/min ASTM D-790 25180 kg/cm2
IZODimpact strength 1/8", 23º C ASTM D-256 25 kg. Cm/cm
Rockwell hardness ASTM D-785 112 R Scale
Thermal properties
Distortion temperature 1/8", 1.8MPa ASTM D-648 80 º C
Vicat softening point 1kg ASTM D-1525 99 º C
Heat of combustion 1/8" UL 94 HB
Physical properties of the flow coefficient 220º C/10kg ASTM D-1238 15.5 g/10min
Proportion: 23º C ASTM D-792 1.045
Mold Shrinkage ASTM D-955 0.5-0.8 %