| Customization: | Available |
|---|---|
| Material: | Ethylene-Vinyl Acetatecopolymers/EVA |
| Usage: | General Plastics |
|
Still deciding? Get samples of US$ 90/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Property Item | Test Method | Test Data | Data Unit |
| Density | ASTM D-1505 | 0.935 | g/cm3 |
| MFR | ASTM D-1238 | 2 | g/10min |
| VA content | ISC.DIS 8965/1989(E) | 14 | % |
| Film Thickness | -- | 40 | u |
| Glossiness | ASTM D-1003A | 82 | % |
| Haze | ASTM D-2457 | 1.9 | % |
| Impact strength | ASTM D-1709 A-B | ≥300 | g |
| Tearing strength(MD) | ASTM D-1922 | 91 | g |
| Tearing strength(TD) | ASTM D-1922 | 129 | g |
| Shore hardness(A) | ASTM D-2240 | 92 | -- |
| Shore hardness(D) | ASTM D-2240 | 33 | -- |
| Tensile yield strength(MD) | ASTM D-638 | 4.5 | N/mm2 |
| Tensile yield strength(TD) | ASTM D-638 | 4.1 | N/mm2 |
| Breaking strength(MD) | ASTM D-638 | 24 | N/mm2 |
| Breaking strength(TD) | ASTM D-638 | 24 | N/mm2 |
| Elongation at break(MD) | ASTM D-6398 | 440 | % |
| Elongation at break(TD) | ASTM D-6398 | 720 | % |
| 1% fracture secant modulus measurement(MD) | ASTM D-882B | 44 | N/mm2 |
| 1% fracture secant modulus measurement(TD) | ASTM D-882B | 50 | N/mm2 |
| Dielectric constant(2×10HZ) | ASTM D-150 | 2.9 | -- |
| Dielectric strength | ASTM D-149 | 670 | KV/cm |
| Vicat softening point | ASTM D-1525 | 70 | °C |
| Melting point | -- | 95 | °C |