Customization: | Available |
---|---|
Material: | Low Density Polyethylene/LDPE |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Project | Test data | Data unit | |
Basic properties | Density | 0.9225 | g/cm3 |
Melt flow rate | 0.75 | g/10min | |
Mechanical properties | HAZE | 9 | % |
Tensile strength | 10 | Mpa | |
Elongation at break | 500 | % | |
Shore hardness | 45 | ||
Thermal properties |
Vicat softening point | 91 | ºC |
Project | Test data | Data unit | ||
Basic properties | Density | 0.920-0.923 | g/cm3 | |
Melt flow rate | 2.1-2.9 | g/10min | ||
Mechanical properties |
Turbidity | ≤30 | % | |
Tensile Strength | crosswise | ≥20 | N/mm | |
length wise direction |
≥50 | N/mm | ||
Cleanliness | ≤7 | Per/kg | ||
Tensile breaking strength |
≥9 | Mpa | ||
Elongation at break | ≥500 | % |
Project | Test method | Test data | Data unit | |
Basic properties | Density | ISO 1183 | 0.922 | g/cm3 |
Melt flow rate | ISO 1133 | 2.0 | g/10min | |
Tensile at yield,MD | ISO 527 | 11 | Mpa | |
Tensile at yield,TD | ISO 527 | 10 | Mpa | |
Mechanical properties | Elongation at break | ISO 527 | 250 | % |
Tensile strength at break | ISO 527 | 26 | Mpa | |
Modulus of Elasticity | ISO 527 | 260 | Mpa- | |
Anti-blocking property | easier | |||
Thermal properties |
Haze | ASTM D-1003 | <7 | % |