Polyoxymethylene POM Injection Grade Dimensional Stability Plastic Raw Materials

• Customization: Available
• Feature: Biodegradable
• CAS No.: 96597-16-9
• Model NO.: pom 057
• Formula: 9002-88-4
• EINECS: 9002-86-2
• Material: Polyacetal/POM
• Usage: General Plastics, Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Delivery: Within 15 Days
• Application: Manufacture Sliding, Rotating Machine Partsr
• Material Color: White
• Place of Origin: China
• Transport Package: 25kg/Bag
• Specification: granule of soybean size
• Trademark: customizable
• Origin: China Mainland
• HS Code: 3907101000
• Production Capacity: 200t/Month

Product Description

Product name:POM granule virgin
Color:White
Origion:China 
Factory address :Hebei,China
Factory experience:20 years

                                                                 TDS

TESTING ITEMS	UNIT	TESTING METHOD	RESULT
density	g/cm3	ISO 1183	1.41
MFI	g/10min	ISO 1133	9
Injection shrinkage rate			2.1-2.9
elongation	%	ISO 527	13-50
water absorption	%	ISO 32	0.2
Tensile modulus	MPa	ISO 527	2700
Rockwell hardness	MPa	ISO 2039	M82(R114)
Standard elongation at break	%	ISO 527	30
Flexural Strength	MPa	ISO 178	61
tensile yield strength	MPa	ISO 527	62
Flexural Modulus	MPa	ISO 178	2400
Notched Izod impact Strength	KJ/m2	ISO 180/1EA	7.5
Charpy Notched Impact Strength	KJ/m2	ISO 179/1EA	7

TESTING ITEMS	UNIT	TESTING STANDARD	RESULT
density	g/cm3	1.40-1.45	1.41
MFI	9g/10min	27	27
tensile strength	mpa	>50	62
elongation	%	>20%	25
tensile modulus	Mpa	2750	2750
Flexural Strength	Mpa	89	89
Flexural modulus	Mpa	2600	2600
IZOD	Kg/m2	4.5	4.5
HDT	ºC	98	98
Flammability		UL-94	HB

Product name:POM granule virgin
Color:White
Origion:China 
Factory address :Hebei,China
Factory experience:20 years

TESTING ITEMS	UNIT	TESTING METHOD	RESULT
density	g/cm3	ISO 1183	1.41
MFI	g/10min	ISO 1133	9
Injection shrinkage rate			2.1-2.9
elongation	%	ISO 527	13-50
water absorption	%	ISO 32	0.2
Tensile modulus	MPa	ISO 527	2700
Rockwell hardness	MPa	ISO 2039	M82(R114)
Standard elongation at break	%	ISO 527	30
Flexural Strength	MPa	ISO 178	61
tensile yield strength	MPa	ISO 527	62
Flexural Modulus	MPa	ISO 178	2400
Notched Izod impact Strength	KJ/m2	ISO 180/1EA	7.5
Charpy Notched Impact Strength	KJ/m2	ISO 179/1EA	7