2022 Hot Saled PC Recycled/Virgin Plastic Materials

• CAS No.: 108-32-7
• Formula: C4h6o3
• EINECS: 232-307-2
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Model NO.: pc-510
• Plastic Forming Method: Blow Molding
• Color: Transparent
• Product: PC
• Packing: 25kg/Bag
• From: China
• White, Black: Color
• Transport Package: in 25kg Bag
• Specification: SGS
• Trademark: Sinopec
• Origin: China
• HS Code: 3901200090
• Production Capacity: 200t/Month

Product Description

Properties:
 
PC is characterized by high transparency, high impact resistance, high hardness, high creep-resistance, excellent dimensional stability, good resistance to low-temperature and heat, flame retardance, ease to process, and excellent sound insulation 
Product description
PC

Item	Test condition	Test method	Data	Unit
Density	25ºC	ASTM D792	1.2	g/cm3
MFR	300ºC 1.2kg	ASTM D1238	7.1-10	g/10min
Tensile strength		ASTM D638	≥60	Mpa
Elastic modulus		ASTM D638	2000-2400	Mpa
Elongation at break		ASTM D638	≥90	%
Charpy Notched Impact Strength		ASTM D6110	≥20	kJ/cm2
Dielectric strength	50HZ	ASTM D149	≥20	Kv/mm
Transparency	2mm	ASTM D1003	≥80	%
VST	50N.50C/h	ASTM D1525	142-146	ºC
Solvent content		GC(int-st)	Max.1500	PPM

 

   PC-0710

Item	Test condition	Test method	Data	Unit
Density	25ºC	ASTM D792	1.2	g/cm3
MFR	300ºC 1.2kg	ASTM D1238	7.1-10	g/10min
Tensile strength		ASTM D638	≥60	Mpa
Elastic modulus		ASTM D638	2000-2400	Mpa
Elongation at break		ASTM D638	≥90	%
Charpy Notched Impact Strength		ASTM D6110	≥20	kJ/cm2
Dielectric strength	50HZ	ASTM D149	≥20	Kv/mm
Transparency	2mm	ASTM D1003	≥80	%
VST	50N.50C/h	ASTM D1525	142-146	ºC
Solvent content		GC(int-st)	Max.1500	PPM

Polycarbonate (English abbreviation PC), also known as PC plastic; It is a polymer containing carbonic acid ester group in the molecular chain. According to the structure of the ester group, it can be divided into aliphatic, aromatic, aliphatic - aromatic and other types. The low mechanical properties of aliphatic and aliphatic aromatic polycarbonate limit their application in engineering plastics.