Properties:
PC is characterized by high transparency, high impact resistance, high hardness, high creep-resistance, excellent dimensional stability, good resistance to low-temperature and heat, flame retardance, ease to process, and excellent sound insulation
Product description
PC
| Item |
Test condition |
Test method |
Data |
Unit |
| Density |
25ºC |
ASTM D792 |
1.2 |
g/cm3 |
| MFR |
300ºC 1.2kg |
ASTM D1238 |
7.1-10 |
g/10min |
| Tensile strength |
|
ASTM D638 |
≥60 |
Mpa |
Elastic modulus |
|
ASTM D638 |
2000-2400 |
Mpa |
| Elongation at break |
|
ASTM D638 |
≥90 |
% |
Charpy Notched Impact Strength |
|
ASTM D6110 |
≥20 |
kJ/cm2 |
Dielectric strength
|
50HZ |
ASTM D149 |
≥20 |
Kv/mm |
| Transparency |
2mm |
ASTM D1003 |
≥80 |
% |
| VST |
50N.50C/h |
ASTM D1525 |
142-146 |
ºC |
| Solvent content |
|
GC(int-st) |
Max.1500 |
PPM |
PC-0710
| Item |
Test condition |
Test method |
Data |
Unit |
| Density |
25ºC |
ASTM D792 |
1.2 |
g/cm3 |
| MFR |
300ºC 1.2kg |
ASTM D1238 |
7.1-10 |
g/10min |
| Tensile strength |
|
ASTM D638 |
≥60 |
Mpa |
| Elastic modulus |
|
ASTM D638 |
2000-2400 |
Mpa |
| Elongation at break |
|
ASTM D638 |
≥90 |
% |
Charpy Notched Impact Strength
|
|
ASTM D6110 |
≥20 |
kJ/cm2 |
Dielectric strength
|
50HZ |
ASTM D149 |
≥20 |
Kv/mm |
| Transparency |
2mm |
ASTM D1003 |
≥80 |
% |
| VST |
50N.50C/h |
ASTM D1525 |
142-146 |
ºC |
| Solvent content |
|
GC(int-st) |
Max.1500 |
PPM |
Polycarbonate (English abbreviation PC), also known as PC plastic; It is a polymer containing carbonic acid ester group in the molecular chain. According to the structure of the ester group, it can be divided into aliphatic, aromatic, aliphatic - aromatic and other types. The low mechanical properties of aliphatic and aliphatic aromatic polycarbonate limit their application in engineering plastics.