Customization: | Available |
---|---|
Material: | Low Density Polyethylene/LDPE |
Usage: | General Plastics |
Still deciding? Get samples of US$ 20/Bag
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Property item | Test condition | Test method | Test data | Data unit |
MFR | 190°C/2.16kg | ISO 1133 | 1.9 | g/10min |
Density | ISO 1183 | 921 | kg/m3 | |
Impulse strength | ASTM D-4272 | 20 | kJ/m | |
Tearing strength(MD) | ISO 6383-2 | 70 | kN/m | |
Tearing strength(TD) | ISO 6383-2 | 25 | kN/m | |
Yield stress(MD) | ISO 527-3 | 11 | MPa | |
Yield stress(TD) | ISO 527-3 | 11 | MPa | |
Fracture stress(MD) | ISO 527-3 | 30 | MPa | |
Fracture stress(TD) | ISO 527-3 | 17 | MPa | |
Elongation at break(MD) | ISO 527-3 | >100 | % | |
Elongation at break(TD) | ISO 527-3 | >500 | % | |
Elasticity modulus(MD) | ISO 527-3 | 190 | MPa | |
Elasticity modulus(TD) | ISO 527-3 | 190 | MPa | |
Frictional factor | ASTM D-1894 | >1 | ||
conglutination | SAB IC method | 20 | g | |
Back conglutination | SAB IC method | 50 | g | |
Gloss | 45 | ASTM D-2457 | 53 | |
Haze | ASTM D-1003A | 10 | % | |
Transparency | SAB IC method | 26 | mV |