Product Parameters
Performance |
Test data |
Data unit |
Melt flow rate |
6-9 |
g/10min |
Izodnotched impact strength |
9.6 |
Kg-cm/cm |
residual monomers |
700 |
ppm |
strength of extension |
195 |
Kg/m2 |
Packing: 25kg/bag
Delivery: Within 15days after receive the advanced payment
Important parameters:
The melt flow rate: 5.5 g / 10 min
Notched impact strength, tensile strength: 22 MPa
Elongation at break: 40%
Bending strength, bending modulus of the 43 MPa: 2260 MPa
Vicat softening point: 95º C
Heat distortion temperature: 88 º C
Project performance
Test conditions [state]
test method
test data
![Directly Warehouse High Impact Polystyrene/HIPS Plastic Granules Best Selling](//www.micstatic.com/athena/img/transparent.png)
HIPS 825
![Directly Warehouse High Impact Polystyrene/HIPS Plastic Granules Best Selling](//www.micstatic.com/athena/img/transparent.png)
![Directly Warehouse High Impact Polystyrene/HIPS Plastic Granules Best Selling](//www.micstatic.com/athena/img/transparent.png)
Product Description
Packing: 25kg/bag
Delivery: Within 15days after receive the advanced payment
Important parameters:
The melt flow rate: 5.5 g / 10 min
Notched impact strength, tensile strength: 22 MPa
Elongation at break: 40%
Bending strength, bending modulus of the 43 MPa: 2260 MPa
Vicat softening point: 95º C
Heat distortion temperature: 88 º C
Project performance
Test conditions [state]
test method
test data
data unit
Melt flow rate
Performance |
Test data |
Data unit |
Melt flow rate |
6-9 |
g/10min |
Izodnotched impact strength |
9.6 |
Kg-cm/cm |
residual monomers |
700 |
ppm |
strength of extension |
195 |
Kg/m2 |