2023 Hot Sale with High Quality ABS for Injection Molding

• Material: Acrylonitrile-Butadiene-Styrene Copolymers/ABS
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film Pressure
• Color: Black
• Processing Method: Injection Molding
• Model NO.: ABS DG417
• Name: ABS
• Transport Package: 25kg/Bag
• Specification: COA
• Trademark: self produce
• Origin: China
• HS Code: 3901200090
• Production Capacity: 100 Tons/Month

Product Description

Acrylonitrile-Butadiene-Styrene(ABS)

virgin & recycled ABS




Description:
ABS appearance is as opaque ivory pellets, non-toxic, odorless, low water absorption, its products can be a variety of colors, and has a 90% high gloss.

ABS is a very good overall performance of the resin, in comparison with a wide range of temperatures, high impact strength and surface hardness, good dimensional stability.

Thermal / mechanical properties:
ABS has excellent mechanical properties, excellent impact strength, can be used at very low temperatures. ABS products are destroyed, it can only be tensile failure without impact damage.

ABS, excellent wear resistance, good dimensional stability, but also has oil resistance, can be used for moderate load and speed of the bearing. ABS flexural strength and compressive strength is less plastic. The mechanical properties of ABS influenced by temperature.

ABS polymers are amorphous, no clear melting point; High melt viscosity, poor fluidity; Very good thermal stability, weather resistance is poor, ultraviolet can change color; The temperature and shear rate are more sensitive.

Application:
ABS resin is mainly used in the automotive, communications equipment, computers, household goods, sporting goods, etc.
 

Performance	Test conditions [state]	Test method	Test data	Data unit
Density	23°C	ASTM D792	1.045	g/cm3
Melt flow rate	220°C/10kg	ASTM D1238	15.5	g/10min
Mold Shrinkage		ASTM D955	0.5-0.8	%
Tensile strength	1/8",50mm/min	ASTM D638	510	kg/cm2
Elongation	1/8",50mm/min	ASTM D638	40	%
Bending strength	1/8",1.3mm/min	ASTM D790	770	kg/cm2
Flexural Modulus	1/8",1.3mm/min	ASTM D790	25180	kg/cm2
Notched Izod impact strength	1/8",23°C	ASTM D256	25	kg/cm2
Rockwell hardness		ASTM D785	112	R Scale
Heat deflection temperature	1/8",1.8MPa	ASTM D648	80	°C
Vicat softening temperature	1kg	ASTM D1525	99	°C
Flame resistance	1/8"	UL94	HB