High Flowability Engineering Plastics POM Granules

• Customization: Available
• Feature: Biodegradable
• CAS No.: 96597-16-9
• Model NO.: pom 057
• EINECS: 9002-86-2
• Material: Polyacetal/POM
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Type: Virgin and Recycled
• Product: Materials
• Material Color: White
• Place of Origin: China
• Transport Package: 25kg/Bag
• Specification: COA
• Trademark: customizable
• Origin: China
• HS Code: 3907101090
• Production Capacity: 500tons/Month

Product Description

POM:
POM/M90/: -->
       

[] ISO 62 0.7 %
ISO 1183 1.41 g/cm3
ISO 32 0.2 %
190ºC,2.16kg ISO 1133 9 g/10min
23ºC ISO 527 13 %
23ºC ISO 527 50 %
358N,30s ISO 2039 140 MPa
24h,4mm 2.8-2.9
  24h,4mm 2.1-2.4
23ºC ISO 527 2700 MPa
23ºC ISO 2039 M82(R114) MPa
  23ºC ISO 527 30 %
23ºC ISO 178 61 MPa
ISO 179/1EA 7 KJ/m2
23ºC ISO 527 62 MPa
  23ºC ISO 178 2400 MPa
ISO 180/1EA 7.5 KJ/m2
  20ºC,50Hz IEC 250 20 ×10-4
21ºC,65%RH ASTM D-495 1.9 mm
20ºC,1KHz IEC 250 10
IEC 93 1015 Ω.cm
  20ºC,1KHz IEC 250 3.9
20ºC,1MHz IEC 250 85
  IEC 112 600 CTI
20ºC IEC 243 25 KV/mm
  20ºC,50Hz IEC 250 3.9
IEC 93 1015 Ω
20ºC,1MHz IEC 250 3.9
  21ºC,65%RH IEC 167 7.5 ×10-4Ω
  1.8MPa ISO 75 115 ºC
  100 ºC
50N ISO 306 B50 150 ºC
  20ºC 1.48 J
10N ISO 306 A50 163 ºC
  ASTM D-696 11 1×10-5K-1
DSC ISO 3146 172 ºC
UL 94(FMVSS) HB(B50)

Item	Test data	Data unit	Test method
Water Absorption	0.7	%	ISO62
Density	1.41	g/cm3	ISO1183
MFI(190ºC,2.16kg)	27	g/10min	ISO1133
Contractility Injection (flow direction)	2.5-2.7
Contractility Injection (vertical)	2.0-2.2
Yield elongation	8	%	ISO527
Elongation at break	20-30	%	ISO527
Tensile modulus	3000	Mpa	ISO527
Bending strength	68	Mpa	ISO178
Tensile yield strength	65	Mpa	ISO527
Flexural modulus	2600	Mpa	ISO178

 

Item	Test data	Data unit	Test method
Water Absorption	0.7	%	ISO62
Density	1.41	g/cm3	ISO1183
MFI(190ºC,2.16kg)	27	g/10min	ISO1133
Contractility Injection (flow direction)	2.5-2.7
Contractility Injection (vertical)	2.0-2.2
Yield elongation	8	%	ISO527
Elongation at break	20-30	%	ISO527
Tensile modulus	3000	Mpa	ISO527
Bending strength	68	Mpa	ISO178
Tensile yield strength	65	Mpa	ISO527
Flexural modulus	2600	Mpa	ISO178