Factory Supply Plastic Material Virgin&Recycled PP Granules

• Customization: Available
• Material: Polypropylene/PP
• Usage: General Plastics
• Model NO.: T30S 66M10T B4808
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film/Injection/Blow/Extrusion
• Color: White
• Type: PP
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Specification: SGS
• Trademark: sinopec
• Origin: China
• HS Code: 3902100090
• Production Capacity: 200t/Month

Product Description

Polypropylene, Virgin PP Granules, PP Plastic Raw Material
 
1.High quality with best price
2.Well reputation
3.Factory with strong supply ability
4. Prompt shipment
 
 Polypropylene PP / Virgin PP Granules/ PP Raw Material
 
Application: 
1)Injection: valve, fittings, crates, automotive, closure, appliances, kettles, food containers, housewares, toys, non-prefilled syringe.
2)Extrusion: thick sheet, sheet, pipe, straw, strapping, Stationery sheet, BOPP Film, thin sheet, band.
3)Blow Molding: bottles.
4)Thermoforming: tray, bowl, jelly cup, water cups.
5)Flat yarn: woven bag, jumbo bag, carpet.
6)Fiber: multifilament, carpet, Spundbond, non-wovens.
7)Film: Cast film (CPP), Blown film (IPP) etc...
 
Specification:

Properties	Unit	Test method	Value
Melt Flow Rate
Melt flow rate(230°C/2.16KG)	g/10min	ISO 1133	12
Mechnical Properties
Tensile modulus of elasticity(v=1mm/min)	Mpa	ISO 527-2	1550
Tensile yield at stress(v=50mm/min)	Mpa	ISO 527-2	35
Tensile yield at strain (v=50mm/min)	%	ISO 527-2	8
Tensile strain at break (v=50mm/min)	%	ISO 527-2	>50
Charpy impact strength unnotched(+23°C)	kJ/m2	ISO 179/1eU	110
Charpy impact strength notched(+23°C)	kJ/m2	ISO 179/1eA	3.0
Izod Impact strength notenched(+23°C)	kJ/m2	ISO 180/1A	3
Ball indentation hardness(H 358/30)	Mpa	ISO 2039-1	78

 
PP Copolymer 

Tests	Value	Unit
Melt Flow Rate	45	g/10min
Density	0.90	G/cm3
Elongation Stress	10	%
Flexural modulus	14	Mpa
Rockwell hardness	95	R scale
IZOD impact strength	6.5	kg.cm/cm
Vicat softening point	152	°C
Heat distortion temperature	125	°C