TESTING ITEMS | UNIT | TESTING METHOD | RESULT |
density | g/cm3 | ISO 1183 | 1.41 |
MFI | g/10min | ISO 1133 | 9 |
Injection shrinkage rate | 2.1-2.9 | ||
elongation | % | ISO 527 | 13-50 |
water absorption | % | ISO 32 | 0.2 |
Tensile modulus | MPa | ISO 527 | 2700 |
Rockwell hardness | MPa | ISO 2039 | M82(R114) |
Standard elongation at break | % | ISO 527 | 30 |
Flexural Strength |
MPa | ISO 178 | 61 |
tensile yield strength | MPa | ISO 527 | 62 |
Flexural Modulus |
MPa | ISO 178 | 2400 |
Notched Izod impact Strength |
KJ/m2 | ISO 180/1EA | 7.5 |
Charpy Notched Impact Strength |
KJ/m2 | ISO 179/1EA | 7 |
TESTING ITEMS | UNIT | TESTING METHOD | RESULT |
density | g/cm3 | ISO 1183 | 1.41 |
MFI | g/10min | ISO 1133 | 9 |
Injection shrinkage rate | 2.1-2.9 | ||
elongation | % | ISO 527 | 13-50 |
water absorption | % | ISO 32 | 0.2 |
Tensile modulus | MPa | ISO 527 | 2700 |
Rockwell hardness | MPa | ISO 2039 | M82(R114) |
Standard elongation at break | % | ISO 527 | 30 |
Flexural Strength |
MPa | ISO 178 | 61 |
tensile yield strength | MPa | ISO 527 | 62 |
Flexural Modulus |
MPa | ISO 178 | 2400 |
Notched Izod impact Strength |
KJ/m2 | ISO 180/1EA | 7.5 |
Charpy Notched Impact Strength |
KJ/m2 | ISO 179/1EA | 7 |