Virgin & Recycled HDPE/High Density Polyethylene Granules Injection/Blow Molding/Extrusion Grade

• Customization: Available
• CAS No.: 9002-88-4
• Formula: C9h18no8p
• Model NO.: HDPE 5502S
• EINECS: 292-752-3
• Material: High Density Polyethylene/HDPE
• Usage: General Plastics
• Plastic Properties After Heated: Thermosetting Plastic
• Plastic Forming Method: Blow Molding
• Color: Translucence
• Type: HDPE
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Specification: international standard
• Trademark: sinopec
• Origin: China
• HS Code: 3901100090
• Production Capacity: 200t/Month

Product Description

HDPE 5502S


Blowing HDPE




Description:
HDPE 5502S is translucence for blowing grade. It's Non-toxic, tasteless, with high impact and good rigidity.

Application:
Used for container filled with the products, like chemical container and other drink bottle.

Item	Test method	Test data	Data unit
Density		0.954	g/cm^3
MFR(190ºC,2.16KG)		2	g/10min
Tensile yield strength		≥27	Mpa
flexural modulus		≥800	Mpa
Elongation at break		≥500	%
Tensile breaking stress		≥21	Mpa

 

Item	Test method	Test data	Data unit
Density		0.954	g/cm^3
MFR(190ºC,2.16KG)		2	g/10min
Tensile yield strength		≥27	Mpa
flexural modulus		≥800	Mpa
Elongation at break		≥500	%
Tensile breaking stress		≥21	Mpa

 

Item	Test method	Test data	Data unit
Density		0.954	g/cm^3
MFR(190ºC,2.16KG)		2	g/10min
Tensile yield strength		≥27	Mpa
flexural modulus		≥800	Mpa
Elongation at break		≥500	%
Tensile breaking stress		≥21	Mpa

Item	Test method	Test data	Data unit
Density		0.954	g/cm^3
MFR(190ºC,2.16KG)		2	g/10min
Tensile yield strength		≥27	Mpa
flexural modulus		≥800	Mpa
Elongation at break		≥500	%
Tensile breaking stress		≥21	Mpa

Item	Test method	Test data	Data unit
Density		0.954	g/cm^3
MFR(190ºC,2.16KG)		2	g/10min
Tensile yield strength		≥27	Mpa
flexural modulus		≥800	Mpa
Elongation at break		≥500	%
Tensile breaking stress		≥21	Mpa