Virgin and Recycled HDPE (8008) Hot Sale

• Customization: Available
• CAS No.: 9002-88-4
• Formula: -[-CH2-CH2-]N-
• Model NO.: HDPE 8008
• EINECS: 37-82-1
• Material: High Density Polyethylene/HDPE
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Application: Injection Molding Grade
• Transport Package: 25kg/Bag
• Specification: SGS
• Origin: Hebe
• HS Code: 3901200090
• Production Capacity: 500tons/Year

Product Description

Technical data sheet
HDPE8008

Description
HDPE 8008 is block copolymer for injection molding with high impact strength
Application
The product can be used for making mechanical parts, containers, sealing material, such as motorcycle fenders, caps, buckets, etc.
Total
Material's state
· Current valid
Performance characteristics
· Eligibility of food contact
Processing method
· Injection molding
Appearance
· White

Property item	Test condition	Test method	Test data	Data unit
MFR	2.16kg	Q/SY DS 0511	7.3	g/10min
Density		Q/SY DS 0510	0.9566	g/cm3
Tensile yield  stress		Q/SY DS 0512	30.4	MPa
Tensile stress  at break		Q/SY DS 0512	26.3	MPa
Tensile stain  at break		Q/SY DS 0512	1481	%
IZOD Impact  Strength		GB/T 1043.1-2008	5.8	kJ/m2

Item	Test method	Test data	Data unit
Density		0.955	g/cm^3
MFR(190ºC,2.16KG)		0.35	g/10min
Tensile yield strength		27	Mpa
flexural modulus		1370	Mpa
Elongation at break		≥600	%
Brittle temperature		≤-75	ºC

Project performance	Test conditions [state]	Test method	Test data	Data unit
Density		ASTM D-1505	0.946	g/cm3
Melt flow rate	190ºC/2.16kg	ASTM D-1238	0.18	g/10min
	190ºC/21.6kg	ASTM D-1238	15	g/10min
Flexural modulus		ASTM D-790	1150	MPa
Falling dart impact strength		ASTM D-1709	90	g
Tensile yield strength		ASTM D-882	MD,24	MPa
			TD, 26
Elongation at break		ASTM D-882	MD,480	%
			TD, 640
Brittle temperature		ASTM D-746	<-75	ºC
Elleman, torn apart		ASTM D-1922	MD,19	g
			TD,270