| Item |
Test condition |
Test method |
Data |
Unit |
| Density |
25ºC |
ASTM D792 |
1.2 |
g/cm3 |
| MFR |
300ºC 1.2kg |
ASTM D1238 |
7.1-10 |
g/10min |
| Tensile strength |
|
ASTM D638 |
≥60 |
Mpa |
| Elastic modulus |
|
ASTM D638 |
2000-2400 |
Mpa |
| Elongation at break |
|
ASTM D638 |
≥90 |
% |
Charpy Notched Impact Strength
|
|
ASTM D6110 |
≥20 |
kJ/cm2 |
Dielectric strength
|
50HZ |
ASTM D149 |
≥20 |
Kv/mm |
| Transparency |
2mm |
ASTM D1003 |
≥80 |
% |
| VST |
50N.50C/h |
ASTM D1525 |
142-146 |
ºC |
| Solvent content |
|
GC(int-st) |
Max.1500 |
PPM |
Description:
PC/SC-1100 homopolymer for injection moulding applications with high transparency and high gloss.
Applications:
The product is used for optic lighting, electronic appliances, mechanical equipment
Optic lighting: Used in the manufacture of large chimney, protective glass also can be used in transparent Material on the plane.
Electronic appliances such as CD, telephones, computers, videos and so on.
Mechanical equipment: Used in the manufacture of all kinds of parts also can be used to make machine Shell and frame.
Others: Can be used for toys, model and so on
Total:
Material's state
Current valid
Performance feature
High transparency
Appearance
Clear/transparency
Processing method
Injection moulding
Property Item
Test Data
Test Method
Density
1.2
ASTM D792
MFR
10g/10min
ASTM D1238
Water absorption
0.2%
ASTM D570
Tensile strength
630kgf/cm2
ASTM D638
Flexural strength(2.8mm/min)
920kgf/cm2
ASTM D790
Flexural modulus(2.8mm/min)
24000kgf/cm2
ASTM D790
Molding shrinkage
0.5-0.7%
ASTM D955
IZOD impact strength(1/8)
87kgf/cm2
ASTM D256
Rockwell hardness
77M
ASTM D785
Distortion temperature(0.45Mpa)
138°C
ASTM D648
Distortion temperature(1.8Mpa)
125°C
ASTM D648
Vicat softening point
150°C
ASTM D1525