Virgin and Recycled Injection General Liquidity PP/ Plastic Material Natural Particle

• Customization: Available
• Feature: Oxidative Degradable
• CAS No.: 12566
• Model NO.: PP EP200K
• Formula: 2563
• EINECS: 5295969
• Material: Polypropylene/PP
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Application: Making Pipe
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Place of Origin: China
• Transport Package: 25kg/PP Bag
• Specification: SGS
• Trademark: self produce
• Origin: China
• HS Code: 3902100090
• Production Capacity: 300t/Month

Product Description

1. Specification
 

Specifications
Melt flow rate	3.5 g/10 min (230°C/2.16kg)
Density	0.903 g/cm³
Tensile Stress at Yield	30MPa
Tensile Strain at Yield	4 %
Flexural modulus	1300 (23 °C)
Charpy notched impact strength	9.0 kJ/m² (23 °C)
Mold shrinkage	1.3

 2.  Properties
 

Properties	Unit	Test method	Value
Melt Flow Rate
Melt flow rate(230°C/2.16KG)	g/10min	ISO 1133	12
Mechnical Properties
Tensile modulus of elasticity(v=1mm/min)	Mpa	ISO 527-2	1550
Tensile yield at stress(v=50mm/min)	Mpa	ISO 527-2	35
Tensile yield at strain (v=50mm/min)	%	ISO 527-2	8
Tensile strain at break (v=50mm/min)	%	ISO 527-2	>50
Charpy impact strength unnotched(+23°C)	kJ/m2	ISO 179/1eU	110
Charpy impact strength notched(+23°C)	kJ/m2	ISO 179/1eA	3.0
Izod Impact strength notenched(+23°C)	kJ/m2	ISO 180/1A	3
Ball indentation hardness(H 358/30)	Mpa	ISO 2039-1	78

 
 
3.  PP Copolymer
 

Tests	Value	Unit
Melt Flow Rate	45	g/10min
Density	0.90	G/cm3
Elongation Stress	10	%
Flexural modulus	14	Mpa
Rockwell hardness	95	R scale
IZOD impact strength	6.5	kg.cm/cm
Vicat softening point	152	°C
Heat distortion temperature	125	°C

 
 
4. PP Random Copolymer (PPR)
 

Tests	Value	Unit	Method
Melt Flow Rate (MFR)	0.45	g/10min	GB 3682
Density	0.91	g/cm3	ASTM D-1505
Tensile Strength at Yield	24	Mpa	GB 1040
Elongation at Break	750	%	GB 1040
Rockwellhardness	85	J/M	GB 9342
Izod impact strength	65	J/M	ASTM D-256

 
 
5.  Application
 
>>  Injection: valve, fittings, crates, automotive, closure, appliances, kettles, food containers, housewares, toys, non-prefilled syringe.
 
>>  Extrusion: thick sheet, sheet, pipe, straw, strapping, Stationery sheet, BOPP Film, thin sheet, band.
 
PP Extrusion Pipe Grade
 

ITEM	Unite	Value	Test Method
Melt Mass-Flow Rate (MFR, 2.16kg)	g/10 min	8	ASTM D-1238
Tensile Strength at Yield (50 mm/min)	MPa	23	ASTM D-638
Elongation at Yield (50 mm/min)	%	7	ASTM D-638
Flexural Modulus (1% secant)	MPa	1050	ASTMD-790A
Notched Izod Impact Strength (23°C)	J/m	150	ASTM D-256
Heat Deflection Temperature (455 kPa)	°C	95	ASTM D648

 
PP Raffia Grade
 

ITEM	Unite	Value	Test Method
Melt Mass-Flow Rate (MFR, 2.16kg)	g/10 min≤	12.3	GB/T 3682
Tensile Strength at yield	MPa≥	30.8	GB/T 1040
Bending modulus	MPa≥	1000	GB/T 9341
Notched Izod impact Strength	(23ºC, KJ/m2)	9.2	GB/T 1843

 
PP Bopp Film Grade
 

ITEM	Unite	Value	Test Method
Melt Mass-Flow Rate	g/10 min	40	GB3682
Density	kg/m3	905	ASTM/D1505
Tensile Strength at Yield	MPa	23	GB1040
Tensile Elongation at Break	%	50	GB1040
Rockwell Hardness		85	GB9342
Heat Deflection Temperature	ºC	105	ASTM/D648
IZOD Impact Strength	(23ºC,J/m)	60	ASTM/D265