Virgin/ Recycled LDPE/LLDPE/HDPE Granules for Film/Extrusion/Injection Grade

• Customization: Available
• Material: Linear Low Density Polyethylene/LLDPE
• Usage: General Plastics
• Model NO.: lldpe 7149
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film/Injection/Blow/Extrusion
• Color: According to Your Demand
• Type: LLDPE
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Specification: SGS
• Origin: China
• HS Code: 3901902000
• Production Capacity: 200t/Month

Product Description

High Quality LLDPE Virgin/Recycled Granules
Fiber (Carpet, Textiles, Upholstery, etc.)
Film (Shopping bags, casting film, multilayer film, etc.)
Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)
Extrusion Molding (Sheet, Pipe, Wire & Cable, etc.)
Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc.
1, LLDPE film grade
 
 

Tests	Value	Unit
Melt Flow Rate (MFR)	2.0±0.4	g/10min
Density	920±2	Kg/cm3
Tensile Strengthat Yield	8	Mpa ≥
Tensile Strengthat Break	12	Mpa ≥
haze	15	%≤
Packing	In 25 kg PP woven bags,20MT/20'FCL

 
2, LLDPE for Master Batch Use
 

Tests	Value	Unit
Melt Flow Rate (MFR)	20	g/10min
Density	0.924	g/cm3
Tensile Strength	MD12	Mpa
	TD 10
Elongation at Yield	13	%
Elongation at Break	200
Dark Drop Impact	105	g
Brittle Temperature(F 50)	-70	°C
Vicat Softening Point	90	°C
Packing	In 25 kg PP woven bags,20MT/20'FCL

 
3, LLDPE Powder Rotational Molding Grade for Tank Use

Tests	Value	Unit
Melt Flow Rate (MFR)	3.2	g/10min
Density	0.939	g/cm3
Melting Point	127	°C
Tensile Yield Strength	21	Mpa
Tensile Strength at Break	28	Mpa
Elongation at Break	1,100	%
Flexural Modulus	750	Mpa
Brittle Temperature	<-60	°C