Raw Material PA6/PA66 Nylon 6 for Injection Molding

• Customization: Available
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics
• Model NO.: PA6 1013B
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Mfr: 15.49g/10min
• Transport Package: 25kg/Bag
• Specification: COA
• Origin: China
• Production Capacity: 800tons/Month

Product Description

 
PA6 1013B is copolymerization for injection molding with the safety
and reliability of the excellent stability.
 
PA6 has high tensile strength, resistance and tough, impact resistant, self-lubricating, wear resistance, chemical resistance, low temperature resistance, etc.

Description: Copolymerization; Injection molding; The excellent stability.

Application: Auto parts, power tools, electrical outlet, building materials.

The product is used for making used in auto parts, power tools,
electrical outlet, building materials.

Material's state: Current valid


 

Total
Material's state		?Current valid
Processing method		?Injection molding
Appearance		?White
Application		?Auto parts,building materials
Physical property	Rating	Test method
Density	1.14 g/cm3
MFR(230ºC,2.16KG)	15.49g/10min	GB/T 3682-2000
Mechanical property	Rating	Test method
Tensile strength	59.21MPa	GB/T 1040-1992
Elongation at break	123.67/v50%	GB/T 1040-1992
Flexural strength	68.79 MPa	GB/T 9341-2000
Flexural modulus	1.51GPa	GB/T 9341-2000
Impact property	Rating	Test method
Charpy Notched Impact Strength	29.51KJ/m2	GB/T 1043-1993
Charpy impact strength	25JNBKJ/m2	GB/T 1043-1993
Other property	Rating	Test method
Relative viscosity deviation	<0.02WT%
Relative viscosity	2.75
Viscosity	2.81	GB/T 1632-1993
Water content	0.06WT%
Tio2content	0-1.3WT%
NOTE ISO 9001 2000

If you need the product ,hope you could contact me anytime, I will offer the detailed information and the competitive price fopr your reference.