LDPE LLDPE HDPE Resins Granules Pellets Chips Compounds Powder Virgin Recycled Reprocessed PE Polyethylene

• CAS No.: 9002-88-4
• Formula: (C2h4)N
• EINECS: 200-815-3
• Material: Polyethylene/PE
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Model NO.: types match-fit or recommended accordingly
• Plastic Forming Method: Film/Molding/Blow/Injection
• Color: Blue White Black Green Customized
• Type: PE, Polyethylene, Virgin, Recycled, Reprocessed
• Payment: T/T, L/C, Wechat, West Union
• Shipping Terms: Fob, CNF, CIF, CPT, Fca
• Departure Port: Tianjin Xingang
• Delivery Lead Time: 7days-15days -30days
• Export Market: South America, Asia, Africa, Europe
• Product Code: Recommended Accordingly, as Per to Requirements
• Shape/Form/Appearance: Resin, Pellets, Chips, Compounds, Regrinds
• Shape/Form/Appearance Extra: Lump, Flake, Waste
• Application/Usage: Film, Caps, Handle, Bottle, Yarn, Bag, Pipe
• Ranking: Top 3 in Made-in-China(Mic)
• Certificate: Co, COA, Quality Inspection
• Standard Compliance: ISO9001, QC080000, CE/FDA
• Shelf Life: 1 Year
• Storage: Keep in Dry Place, Sealed.
• Transport Package: Bag 25kg/Bag Jumbo Bag, with Pallete, Customizable
• Specification: granule of soybean size
• Trademark: self produce, SINOPEC, CUSTOMIZABLE
• Origin: China Mainland, Prc, People′s Republic of China
• HS Code: 3901100090
• Production Capacity: 5000t/Year, 200-300t/Month

Product Description

PRODUCT NAME:PE POLYETHYLENE 
TYPE:VIRGIN&RECYCELED(REPROCESSED)
PRICE:FACTORY PRICE,COMPETITIVE,
QUALITY:GOOD.PRIME,HIGH
INDUSTRY EXPERIENCE :MORE THAN 15 YEARS
FACTORY LOCATION:HEBEI,NORTH CHINA,PRC
DELIVERY LEAD TIME:15DAYS USUALLY-30DAYS DURING PEAK SEASON
AFTER SALES SERVICE:GOOD
TDS:
1.FILM



2.BOTTLE

Item	Test method	Test data	Data unit
Density		0.963-0.967	g/cm^3
MFR(190ºC,2.16KG)		5.80	g/10min
Tensile yield strength		200	Kg/cm2
Powder ash		0.04	wt%
Elongation at break		500	%

3.CAPS

Item	Test method	Test data	Data unit
Density	GB/T1033- 1986	0.956	g/cm3
MFR(190ºC,2.16KG)	GB/T3682- 2000	2.2	g/10min
Tensile yield strength	GB/T1410/ 1992	24.0	Mpa
Elongation at break	GB/T1410/ 1992	600	%
IZOD Impact Strength	GB/T1413/ 1993	13	Kg/m2
Flexural modulus	GB/T1843- 1996	1000	Mpa

4.HANDLES

Item	Test method	Test data	Data unit
Density		0.963	g/cm3
MFR		8.2	g/10min
Tensile yield strength		≥10.0	Mpa
Tensile breaking strength		≥30.0	Mpa
Elongation at break		≥140	%

5.BAG


6.PIPE

Item		Test method	Test data	Data unit
Density		GB/T 1033	0.948	g/cm3
MFR	190ºC/5.0kg	GB/T 3682	0.25	g/10min
	190ºC/21.6kg	GB/T 3682	6.4
Tensile yield strength		GB/T 1040	≥23	Mpa
Volatile component		GB/T156581	≤ 350	Mg/kg
Elongation at break		GB/T 1040	≥600	%
CHARPY Impact Strength		GB/T 1043	≥25	KJ/m2
Cleanliness(colored particle)		SH/T 1541	≤ 20	Per/kg
Cleanliness(impurities)		SH/T 1541	≤ 60	Per/kg