Plastic Raw Material PA6 /Nylon 6 Injection Molding

• Customization: Available
• CAS No.: 5911-08-0
• Formula: -[CH2-CH2]N-
• Model NO.: PA6 1013B
• EINECS: 5911-08-0
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Mfr: 15.49g/10min
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Specification: SGS
• Origin: China
• HS Code: 3904109090
• Production Capacity: 500tons/Month

Product Description

PA6 has high tensile strength, resistance and tough, impact resistant, self-lubricating, wear resistance, chemical resistance, low temperature resistance, etc.

Description: Copolymerization; Injection molding; The excellent stability.

Application: Auto parts, power tools, electrical outlet, building materials.

Material's state: Current valid

Appearance: White

Property item	Test condition	Test method	Test data	Data unit
Density                                                   Relative viscosity deviation			1.14       <0.02	g/cm3 WT%
Relative viscosity			2.75
MFR	230°C,2.16KG	GB/T 3682-2000	15.49	g/10min
Viscosity		GB/T 1632-1993	2.81
Charpy Notched Impact Strength		GB/T 1043-1993	29.51	KJ/m2
Charpy impact strength		GB/T 1043-1993	25JNB	KJ/m2
Tensile strength		GB/T 1040-1992	59.21	MPa
Elongation at break		GB/T 1040-1992	123.67/v50	%
Flexural strength		GB/T 9341-2000	68.79	MPa
Flexural modulus		GB/T 9341-2000	1.51	GPa

Grade
Injection grade
Data sheet      

Performance	Test Method	Test data	Data unit
Water absorption	ASTM D-570	1.8	%
Density	ASTM D-792	1.14	g/cm3
Tensile strength	ASTM D-638	400	kgf/cm2
Flexural Modulus	ASTM D-790	1300	kgf/cm2
Impact strength	ASTM D-256	50	kgf.cm/cm
Hardness	ASTM D-785	55
Melting point		215-225	ºC
HDT	ASTM D-648	75	ºC