| Data sheet | |||||||
| Item | Test method | Test data | Data unit | ||||
| MFR | ASTM D-1238 | 12 | g/10min | ||||
| Density | ASTM D-792 | 1.03 | g/cm3 | ||||
| IZOD | ASTM D-256 | 36 | Kg.cm/cm | ||||
| Tensile breaking | ASTM D-638 | 385 | Kg/cm2 | ||||
| strength | |||||||
| Tensile Elongation | ASTM D-648 | 30 | % | ||||
| yield | |||||||
| Hardness | ASTM D-785 | 108 | R | ||||
| Vicat | ASTM D-1525 | 103 | ºC | ||||
| Item | Test method | Test data | Data unit |
| MFR (220ºC 10kg) |
ASTM D-1238 | 23 | g/10min |
| Density(23ºC) | ASTMD-792 | 1.05 | g/cm3 |
| Water absorption(23ºC,24hr) | ASTM D-570 | 0.3 | % |
| Mold shrinkage rate | ASTM D-955 | 0.3-0.5 | % |
| Flexural Modulus(5mm/min) | ASTM D-790 | 26000 | kg/cm² |
| Flexural Strength(5mm/min) | ASTM D-790 | 800 | kg/cm² |
| Elongation(50mm/min) | ASTM D-638 | 18 | % |
| Tensile strength(50mm/min) | ASTM D-638 | 500 | kg/cm² |
| Heat Deflection Temperature(18.6kg/cm²) | ASTM D-259 | 93 | ºC |
| Vicat Softening Temperature(5kg 50ºC/nr) | ASTM D-1525 | 103 | ºC |
| IZOD Impact Strength | ASTM D256 | 22 | kg-cm/cm |
| Rockwell hardness | ASTM D785 | 109 | |
| Whiteness index(Cyan reflectance method) | 53 | ||
| Glossiness (45ºC) | 104 | ||
| UL flame retardant grade(all color) | UL94 | HB |
| Item | Test method | Test data | Data unit | ||||
| MFR (220ºC10kg) | ASTM D-1238 | 20 | g/10min | ||||
| Density | ASTM D-792 | 10.4 | g/cm³ | ||||
| Water absorbing | ASTM D-570 | 0.3 | % | ||||
| Shrinkage of molding (12×15×10mm) |
ASTM D-955 | 0.3-0.6 | % | ||||
| Yield elongation | ASTM D-638 | 2.7 | % | ||||
| Elongation at break | ASTM D-638 | 20 | % | ||||
| Tensile modulus | ASTM D-638 | 23500 | kg/cm² | ||||
| Flexural Modulus | ASTM D-790 | 24000 | kg/cm² | ||||
| Tensile yield strength | ASTM D-638 | 470 | kg/cm² | ||||
| Tensile breaking strength | ASTM D-638 | 430 | kg/cm² | ||||
| Flexural Strength | ASTM D-790 | 700 | kg/cm² | ||||
| Thermal conductivity -80ºC | DIN 52612 | 0.17 | W/(K.m) | ||||
| Distortion temperature 1.8MPa(HDT A) | ASTM D-648 | 101 | °C | ||||
| Vicat softening point | ISO 306 | 97 | °C | ||||
| Notched impact strength of cantilever beam 23ºC | ISO 180/1U | 25 | kJ/m² | ||||
| UL flame retardant grade | UL 94 | HB | |||||
| Rockwell hardness | ASTM D-785 | 103 | |||||