1. Description:
PP EP200K is copolymer for injection moulding.
2. Application:
PP EP200K used for car accessories, commodity like hanger chair drum and so on, electrical equipment, Film and pipe.
3. Total:
Material's state · Current valid
Performance characteristics · Eligibility of food contact
Processing method · Injection extrusion molding
Appearance · White
| Property Item |
Test Data |
Test Method |
| MFR (2.16kg) |
3.19 g/10min |
GB/T 3682-2000 |
| Rockwell hardness |
87R |
GB/T 3398.2-2008 |
| Molding shrinkage(parallel) |
1.6% |
GB/T 17037.4-2003 |
| Molding shrinkage(vertical) |
1.7% |
GB/T 17037.4-2003 |
| Flexural modulus |
1105MPa |
GB/T 9341-2000 |
| Tensile stress at Yield |
23Mpa |
GB/T 1040.2-2006 |
| Charpy Notched Impact Strength(23°C) |
20 Kj/m2 |
GB/T 1043-2008 |
| Charpy Notched Impact Strength(-20°C) |
8.4 Kj/m2 |
GB/T 1043-2008 |
| Distortion temperature(0.45MPa) |
76 °C |
GB/T 1634.1-2004 |
PP 66m10t
Data sheet
| Item |
Test method |
Test data |
Data unit |
| Density |
ASTM D-792 |
0.905 |
g/cm3 |
| MFR |
ASTM D-1238 |
3.5 |
g/10min |
| Tensile yield strength |
ASTM D-638 |
23 |
Mpa |
| The yield tensile elongation |
ASTM D-638 |
10 |
% |
| Rockwell hardness |
ASTM D-785 |
80 |
% |
| notched izod impact strength |
-20ºC |
ASTM D-256 |
100 |
J |
| 23ºC |
ASTM D-256 |
750 |
J/m |
| Flexural modulus |
ASTM D-790A |
1000 |
Mpa |
| HDT |
ASTM D-648 |
85 |
ºC |
| Vicat Softening Temperature |
ASTM D-1525B |
145 |
ºC |
){kind=link}