PVC Sg3, Sg5, Sg8 Raw Material/ Virgin/ PVC Resin Hot on Sale

• Customization: Available
• Material: Polyvinyl Chloride/PVC
• Usage: General Plastics
• Model NO.: sg3 sg5 sg8
• Plastic Forming Method: Film/Injection/Blow/Extrusion
• Color: Transparent
• Type: PVC
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Specification: SGS
• Trademark: sinopec
• Origin: China
• HS Code: 3904109090
• Production Capacity: 200t/Month

Product Description

Hard PVC
Feed tube temperature: 160-190 ºC
Mold temperature: 40 to 60 ºC
The drying temperature: 80 ºC x2h
Shoot rubber pressure: 700-1500 kg/c m2
Density: 1.4 g/c m2
Molding shrinkage degree: 0.1 to 0.5%
Thick meat: 2.0-50 mm
Bibulous rate (24 h) : 0.1-0.4%
Melting degree of softening point: 89 ºC
The thermal deformation temperature: 70 ºC
 
Soft PVC
 
Feed tube temperature: 140-170 ºC
 
Mold temperature: 40 to 60 ºC
 
The drying temperature: 80 ºC x2h
 
Shoot rubber pressure: 600-1500 kg/c m2
 
Density: 1.4 g/c m2
 
Molding shrinkage degree: 0.1 to 0.5%
 
Thick meat: 2.0-50 mm
 
Bibulous rate (24 h) : 0.1-0.4%
 
Melting degree of softening point: 85 ºC
 
Thermal deformation temperature: 55 ºC
Sample Property:
 
 
 

PROPERTY	UNIT		TEST
		JR-70
Tensile strength at aging	Mpa	16.8	GB1040
Elongation at break	%	310	GB1040
Thermal agining 100°C 168h	--	--	--
tensile strength at aging	Mpa	16	GB1040
Maximum change rate of Tensile Strength	%	-4.8	--
Elongation ate Break after aging	%	290	GB1040
Maximum change rate of Elongation at break	%	-6.5	--
Weight Loss after Thermal aging	g/cm3	11.2	--
Thermal deformation	%	35	--
Brittle point of Low temperature impact	°C	(-)40pass	GB5470
Thermal stable time at 20°C	min	95	--
Volume resistivity at 20°C	Ω.m	2.2*1013	GB1410
Volume resistivity at working time of 20°C	Ω.m	3.5*109	GB1410
Dielectronic strength	mv/m	27	GB1408