Recycled &Virgin HDPE Granule with Factory Price

• CAS No.: 9002-88-4
• Formula: -[-CH2-CH2-]N-
• EINECS: 260(65603-19-2)
• Material: High Density Polyethylene/HDPE
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Model NO.: HDPE 5502s
• Plastic Forming Method: Film Pressure
• Color: White
• Application: Used for Making Bags
• Transport Package: 25kg/Bag
• Specification: COA
• Trademark: self produce
• Origin: China
• HS Code: 3901200090
• Production Capacity: 300

Product Description

ProductHDPE
Specification levelFilm grade
ApplicationProduct bag shopping bag multilayer the lining of bags and garbage bags, etc.
Density0.937 g/cm3 MFI0.13 g/10min tensile strength19MPa
E longation at break 600 % notch impact strength 160 Vicat softening point120

Performance of the project Test conditions [state] test data data unit
Density ASTM D-1505 0.937 g/cm3
MFR ASTM D-1238 0.15 g/10min
Flexural modulus ASTM D-790 1103 MPa
Falling dart impact strength ASTM D-1709 100 g
Tensile yield strength ASTM D-882MD, TD, 26, 25 MPa
Tensile strength ASTM D-882MD, TD, 32, 31 MPa
Elongation at break ASTM D-882TD, MD, 600, 500 %
Typical blown film performance 0.025mm 4: 1
Elleman, torn apart ASTM D-1922MD, TD 26, 410 g

Item	Test method	Test data	Data unit
Density		0.954	g/cm^3
MFR(190ºC,2.16KG)		2	g/10min
Tensile yield strength		≥27	Mpa
flexural modulus		≥800	Mpa
Elongation at break		≥500	%
Tensile breaking stress		≥21	Mpa

Item	Test data	Data unit
Density	0.949-0.953	g/cm3
MFR(190ºC,2.16KG)	0.80-1.10	g/10min
Tensile yield strength	≥24.0	Mpa
Powder ash	≤0.01	%(m/m)
Elongation at break	≥500	%
cleanliness(colored particle)	≤5	granule/kg resin
cleanliness(impurity)	≤ 20	granule/kg resin