Hot Sale PA6/ PA66/Polyamide with High Quality

• Customization: Available
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Model NO.: virgin grade
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White Transparent
• Processing Method: Injection Molding
• Application: Auto Parts, Building Materials
• Transport Package: in 25kg/Bag or Jumbo Bag
• Specification: COA
• Trademark: Sinopec
• Origin: China Mainland
• HS Code: 3901200090
• Production Capacity: 200 Tons/ Month

Product Description

Description
PA6 1013B is copolymerization for injection molding with the safety
And reliability of the excellent stability.


Application

The product is used for making used in auto parts, power tools,
Electrical outlet, building materials

Physical property	Rating	Test method
Density	1.14 g/cm3
MFR(230 ºC,2.16KG)	15.49g/10min	GB/T 3682-2000
Mechanical property	Rating	Test method
Tensile strength	59.21MPa	GB/T 1040-1992
Elongation at break	123.67/v50%	GB/T 1040-1992
Flexural strength	68.79 MPa	GB/T 9341-2000
Flexural modulus	1.51GPa	GB/T 9341-2000
Impact property	Rating	Test method
Charpy Notched Impact Strength	29.51KJ/m2	GB/T 1043-1993
Charpy impact strength	25JNBKJ/m2	GB/T 1043-1993
Other property	Rating	Test method
Relative viscosity deviation	<0.02WT%
Relative viscosity	2.75
Viscosity	2.81	GB/T 1632-1993
Water content	0.06WT%
Tio2content	0-1.3WT%
NOTE ISO 9001 2000
Typical properties: these are not to be construed as specifications