Copolyformaldehyde POM M90 Polyoxymethylene pom resin Acetal Copolymer Descriptions: 1) High flow, high wear resistance and high strength 2)Antibacterial, acid resistance, alkali resistance, high hardness, good chemical stability Application: Electrical and electronic equipment, accessories, thin wall parts, car accessories, gear, valve parts, car inner decoration, pipeline, roller, bearing, pump parts.
Property Item |
Test Condition |
Test Data |
Test Method |
Density |
|
1.14g/cm3 |
ISO 1183 |
MFR |
(190°C/2.16kg) |
9 g/10min |
ISO 1133 |
Tensile strength(yield) |
|
62Mpa |
ISO 527 |
Tensile modulus |
|
2700Mpa |
ISO 527 |
Flexural strength |
|
61Mpa |
ISO 178 |
Flexural modulus |
|
2400Mpa |
ISO 178 |
Elongation(yield) |
|
13% |
ISO 527 |
Elongation at break |
|
30% |
ISO 527 |
Notched IZOD impact strength |
|
7.5Kj/m² |
ISO 180/1eA |
Charpy Notched Impact Strength |
|
7.5Kj/m² |
ISO 179/1EA |
Ball-indentation hardness |
(H 358/30) |
140Mpa |
ISO 2039 |
Rockwell hardness |
(23°C) |
114R |
ISO 2039 |
Distortion temperature |
(1.8Mpa) |
115°C |
ISO 75 |
Vicat softening point |
(50N) |
150°C |
ISO 306/B50 |
Vicat softening point |
(10N) |
163°C |
ISO 306/A50 |
Melting point |
|
172°C |
ISO 3146 |