TESTING ITEMS |
UNIT |
TESTING STANDARD |
RESULT |
density |
g/cm3 |
1.40-1.45 |
1.41 |
MFI |
9g/10min |
27 |
27 |
tensile strength |
mpa |
>50 |
62 |
elongation |
% |
>20% |
25 |
tensile modulus |
Mpa |
2750 |
2750 |
Flexural Strength |
Mpa |
89 |
89 |
1. Description:
POM M90 is a copolymer for injection molding.
2. Applications:
The product used in manufacture of auto part
3. Total:
Material's state Current valid
Application Auto part
Appearance White
Processing method Injection molding
Property Item |
Test Condition |
Test Data |
Test Method |
Density |
|
1.14g/cm3 |
ISO 1183 |
MFR |
(190°C/2.16kg) |
9 g/10min |
ISO 1133 |
Tensile strength(yield) |
|
62Mpa |
ISO 527 |
Tensile modulus |
|
2700Mpa |
ISO 527 |
Flexural strength |
|
61Mpa |
ISO 178 |
Flexural modulus |
|
2400Mpa |
ISO 178 |
Elongation(yield) |
|
13% |
ISO 527 |
Elongation at break |
|
30% |
ISO 527 |
Notched IZOD impact strength |
|
7.5Kj/m² |
ISO 180/1eA |
Charpy Notched Impact Strength |
|
7.5Kj/m² |
ISO 179/1EA |
Ball-indentation hardness |
(H 358/30) |
140Mpa |
ISO 2039 |
Rockwell hardness |
(23°C) |
114R |
ISO 2039 |
Distortion temperature |
(1.8Mpa) |
115°C |
ISO 75 |
Vicat softening point |
(50N) |
150°C |
ISO 306/B50 |
Vicat softening point |
(10N) |
163°C |
ISO 306/A50 |
Melting point |
|
172°C |
ISO 3146 |