Virgin POM Polyoxymethylene (M90) for Injection Molding Plastic Material

• Customization: Available
• Formula: -[CH2-CH2]N-
• Material: Polyacetal/POM
• Model NO.: POM M90
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Mfr: 9 G/10min
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Specification: SGS
• Origin: China
• HS Code: 3904109090
• Production Capacity: 800tons/Month

Product Description

 

TESTING ITEMS	UNIT	TESTING STANDARD	RESULT
density	g/cm3	1.40-1.45	1.41
MFI	9g/10min	27	27
tensile strength	mpa	>50	62
elongation	%	>20%	25
tensile modulus	Mpa	2750	2750
Flexural Strength	Mpa	89	89

1. Description:
POM M90 is a copolymer for injection molding.
2. Applications:
The product used in manufacture of auto part
3. Total:
Material's state Current valid
Application Auto part
Appearance White
Processing method Injection molding

Property Item	Test Condition	Test Data	Test Method
Density		1.14g/cm3	ISO 1183
MFR	(190°C/2.16kg)	9 g/10min	ISO 1133
Tensile strength(yield)		62Mpa	ISO 527
Tensile modulus		2700Mpa	ISO 527
Flexural strength		61Mpa	ISO 178
Flexural modulus		2400Mpa	ISO 178
Elongation(yield)		13%	ISO 527
Elongation at break		30%	ISO 527
Notched IZOD impact strength		7.5Kj/m²	ISO 180/1eA
Charpy Notched Impact Strength		7.5Kj/m²	ISO 179/1EA
Ball-indentation hardness	(H 358/30)	140Mpa	ISO 2039
Rockwell hardness	(23°C)	114R	ISO 2039
Distortion temperature	(1.8Mpa)	115°C	ISO 75
Vicat softening point	(50N)	150°C	ISO 306/B50
Vicat softening point	(10N)	163°C	ISO 306/A50
Melting point		172°C	ISO 3146