Polycarbonate Plastic Suppliers Resin Raw Materials 120110

• Customization: Available
• Feature: Photodegradable
• CAS No.: 8052-43-5
• Model NO.: pc 1080
• Formula: C40h82no9p
• EINECS: 232-307-2
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Transparency
• Product: Chemicals
• Material Color: White
• Package: 25kg/Bag
• Place of Origin: China
• Transport Package: 25kg/Bag
• Specification: PC
• Trademark: customizable
• Origin: China
• HS Code: 3901200090
• Production Capacity: 300

Product Description

Project	Test Condition	Test Data	Data Unit
MFI	ASTM D-1238	10	g/10min
Density	ASTM D-792	1.2
Mold shrinkage	ASTM D-955	0.5-0.7	%
water absorption	ASTM D-570	0.2	%
Tensile Strength	ASTM D-638	630	Kg/cm2
Elongation	ASTM D-638	110	%
Flexural Strength	ASTM D-790	920	Kg/cm2
Flexural Modulus	ASTM D-790	24000	Kg/cm2
Rockwell hardness	ASTM D-785	77
Notched impact strength	ASTM D-256	87	kg-cm/cm
Volume resistivity	ASTM D-257	3	ohms·cm
Vicat softening temperature	ASTM D-1525	153	°C
Haze	ASTM D-1003	<0.8	%
Refractive index	ASTM D-542	1.585

Description:

PC/SC-1100 homopolymer for injection moulding applications with high transparency and high gloss.

Applications:
The product is used for optic lighting, electronic appliances, mechanical equipment
Optic lighting: Used in the manufacture of large chimney, protective glass also can be used in transparent Material on the plane.
Electronic appliances such as CD, telephones, computers, videos and so on.
Mechanical equipment: Used in the manufacture of all kinds of parts also can be used to make machine Shell and frame.
Others: Can be used for toys, model and so on

Total:
Material's state
Current valid

Performance feature
High transparency

Appearance
Clear/transparency

Processing method
Injection moulding
Property Item
Test Data
Test Method
Density
1.2
ASTM D792
MFR
10g/10min
ASTM D1238
Water absorption
0.2%
ASTM D570
Tensile strength
630kgf/cm2
ASTM D638
Flexural strength(2.8mm/min)
920kgf/cm2
ASTM D790
Flexural modulus(2.8mm/min)
24000kgf/cm2
ASTM D790
Molding shrinkage
0.5-0.7%
ASTM D955
IZOD impact strength(1/8)
87kgf/cm2
ASTM D256
Rockwell hardness
77M
ASTM D785
Distortion temperature(0.45Mpa)
138°C
ASTM D648
Distortion temperature(1.8Mpa)
125°C
ASTM D648
Vicat softening point
150°C
ASTM D1525