Virgin Polyethylene HDPE for Durable and Eco-Friendly Bottles

• Customization: Available
• CAS No.: 9002-88-4
• Formula: -[-CH2-CH2-]N
• Model NO.: HDPE 5502; 5000S, 7000f
• EINECS: 9002-88-4
• Material: High Density Polyethylene/HDPE
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film/Blow/Injection/Extrusion
• Color: According to Your Demand
• Type: HDPE
• Payment: T/T L/C
• Delivery: Wihin 10 Days After Receiving Deposit
• Package: 25kg/Bag
• Transport Package: 25kg/Bag
• Specification: international standard
• Trademark: Self-produced
• Origin: China
• HS Code: 3901902000
• Production Capacity: 500t/Month
• Package Size: 80.00cm * 55.00cm * 25.00cm
• Package Gross Weight: 25.000kg

Product Description

Product Description

1.Pictures

2. Virgin HDPE Granules Characteristic
Our Virgin Polyethylene HDPE granulate boasts exceptional attributes perfect for various applications. This extrusion and pipe-grade material is renowned for its superb weather resistance and impeccable black carbon dispersion. Engineered for excellence, it offers outstanding resistance to both rapid crack propagation and slow crack growth, ensuring longevity and reliability in your products.

3. Virgin & Recycled PE Granules

1>. Blow Molding Grade: Tailored for creating robust, uniform hollow shapes, our blow molding grade is the ideal choice for high-quality, durable bottles and containers.

2>. Injection Molding Grade: This versatile grade is perfect for crafting precise and detailed molded products, ensuring superior performance and finish.

3>. Film Grade: Specially formulated to produce strong, flexible films, this grade is excellent for packaging solutions, providing protection and durability.

4>. Extrusion Grade: Designed for creating consistent, high-quality profiles, our extrusion grade ensures smooth production processes and outstanding outcomes.
4. Specification

HDPE cable material Property	Unit	Typical Value
Mass density	g/cm³	0.941-0.959
Melt flow Rate(190 Centigrade /2.16kg)	g/10min	≤1.0
Tensile yield strength	MPa	≥19.0
Flexural modulus	Mpa	≥965
Elongation@ break	%	≥400
Impact Embrittlement temperature	Centigrade	MAX -118
Dielectric Constant	100KHZ	2.32
	1MHZ	2.31
Loss Tangent	100KHZ	MAX 0.0001
	1MHZ	MAX 0.0001
Volume resistivity	OHM-CM	MIN 1x10 15

Item	Test method	Test data	Data unit
MFR(190ºC,2.16KG)	ASTM D1238	0.3	g/10min
Density	ASTM D792	0.956	g/cm³
Tensile yield strength	ASTM D638	25	Mpa
Tensile breaking strength	ASTM D638	38	Mpa
flexural modulus (2% secant)	ASTM D790	860	Mpa
Elongation at break	ASTM D638	950	%
Environmental stress cracking resistance (50°C, 100% Igepal, F50)	ASTM D1693	>200	hr
Vicat softening point	ASTM D1525	128	ºC
Notched impact strength of cantilevered beams(23ºC)	ASTM D256	130	J/m
Shore hardness(D)	ASTM D2240	66