HDPE 5502S
Blowing HDPE
Description:
HDPE 5502S is translucence for blowing grade. It's Non-toxic, tasteless, with high impact and good rigidity.
Application:
Used for container filled with the products, like chemical container and other drink bottle.
| Item |
Test method |
Test data |
Data unit |
| Density |
|
0.954 |
g/cm3 |
| MFR(190ºC,2.16KG) |
|
2 |
g/10min |
| Tensile yield strength |
|
≥27 |
Mpa |
| flexural modulus |
|
≥800 |
Mpa |
| Elongation at break |
|
≥500 |
% |
| Tensile breaking stress |
|
≥21 |
Mpa |
| Item |
Test method |
Test data |
Data unit |
| Density |
|
0.954 |
g/cm3 |
| MFR(190ºC,2.16KG) |
|
2 |
g/10min |
| Tensile yield strength |
|
≥27 |
Mpa |
| flexural modulus |
|
≥800 |
Mpa |
| Elongation at break |
|
≥500 |
% |
| Tensile breaking stress |
|
≥21 |
Mpa |
| Item |
Test method |
Test data |
Data unit |
| Density |
|
0.954 |
g/cm3 |
| MFR(190ºC,2.16KG) |
|
2 |
g/10min |
| Tensile yield strength |
|
≥27 |
Mpa |
| flexural modulus |
|
≥800 |
Mpa |
| Elongation at break |
|
≥500 |
% |
| Tensile breaking stress |
|
≥21 |
Mpa |
| Item |
Test method |
Test data |
Data unit |
| Density |
|
0.954 |
g/cm3 |
| MFR(190ºC,2.16KG) |
|
2 |
g/10min |
| Tensile yield strength |
|
≥27 |
Mpa |
| flexural modulus |
|
≥800 |
Mpa |
| Elongation at break |
|
≥500 |
% |
| Tensile breaking stress |
|
≥21 |
Mpa |
| Item |
Test method |
Test data |
Data unit |
| Density |
|
0.954 |
g/cm3 |
| MFR(190ºC,2.16KG) |
|
2 |
g/10min |
| Tensile yield strength |
|
≥27 |
Mpa |
| flexural modulus |
|
≥800 |
Mpa |
| Elongation at break |
|
≥500 |
% |
| Tensile breaking stress |
|
≥21 |
Mpa |