Plastic Raw Material PVC Granules Recycled PVC Granules

• Material: Polyvinyl Chloride/PVC
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film/Injection/Blow/Extrusion
• Color: According to You Demand
• Type: PVC
• Model NO.: sg3 sg5 sg8
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Trademark: sinopec
• Origin: China
• HS Code: 3904109090
• Production Capacity: 200 Tons/Month

Product Description

Specification:
 

Items		Unit	Index
			SG1	SG2	SG3	SG4	SG5	SG6	SG7
Viscosity No.		ml/g	156-144	143-136	135-127	126-119	118-107	106-96	95-87
Or K value			76-75	74-73	72-71	70-69	68-66	65-63	62-60
Or Average degree of polymerization			----	---	1350-1250	1250-1150	1100-1000	950-850	750-650
Foreign Particle			30max	30max	30max	30max	30max	30max	40max
Volatile Matter		%	0.4max	0.4max	0.4max	0.4max	0.4max	0.4max	0.4max
Apparent Density		g/ml	0.42min	0.42min	0.42min	0.42min	0.45min	0.45min	0.45min
Particle size	0.25mm Sieve	%	2.0max	2.0max	2.0max	2.0max	2.0max	2.0max	2.0max
	0.063mm Sieve		90min	90min	90min	90min	90min	90min	90min
No. of fish eye		/400cm2	40 max	40 max	40 max	40 max	40 max	50 max	50 max
Plasticizer absorption of 100g resin		g	25min	25 min	25min	22 min	19 min	16min	14min
VCM Residue		ppm	10 max	10 max	10 max	10 max	10 max	10 max	10 max

 
Sample Property:
 

PROPERTY	UNIT		TEST
		JR-70
Tensile strength at aging	Mpa	16.8	GB1040
Elongation at break	%	310	GB1040
Thermal agining 100°C 168h	--	--	--
tensile strength at aging	Mpa	16	GB1040
Maximum change rate of Tensile Strength	%	-4.8	--
Elongation ate Break after aging	%	290	GB1040
Maximum change rate of Elongation at break	%	-6.5	--
Weight Loss after Thermal aging	g/cm3	11.2	--
Thermal deformation	%	35	--
Brittle point of Low temperature impact	°C	(-)40pass	GB5470
Thermal stable time at 20°C	min	95	--
Volume resistivity at 20°C	Ω.m	2.2*1013	GB1410
Volume resistivity at working time of 20°C	Ω.m	3.5*109	GB1410
Dielectronic strength	mv/m	27	GB1408

 
 
Usage:
1. pvc soft products. It can be made of hoses, cables, wires, plastic sandals, shoes, slippers, toys, auto parts etc.
 
2. pvc film. The transparent film can be used for greenhouses, plastic greenhouses and plastic film mulch. It can also be used for packaging bags,      raincoat, table cloth, curtains, inflatable toys etc.
 
3. pvc coated products.  Can be used to make leather luggage, purses, book covers, sofa and car seat,etc. As well as floor covering, flooring materials for buildings.
 
4. pvc foam products. Can be used for foam slippers, sandals, insoles, and anti-vibration cushioning packaging material, Rigid PVC sheet and profiles, it is a new building material.