PA6 1013B is copolymerization for injection molding with the safety
and reliability of the excellent stability.
PA6 has high tensile strength, resistance and tough, impact resistant, self-lubricating, wear resistance, chemical resistance, low temperature resistance, etc.
Description: Copolymerization; Injection molding; The excellent stability.
Application: Auto parts, power tools, electrical outlet, building materials.
The product is used for making used in auto parts, power tools,
electrical outlet, building materials.
Material's state: Current valid
| Total |
| Material's state |
?Current valid |
| Processing method |
?Injection molding |
| Appearance |
?White |
| Application |
?Auto parts,building materials |
| Physical property |
Rating |
Test method |
| Density |
1.14 g/cm3 |
| MFR(230ºC,2.16KG) |
15.49g/10min |
GB/T 3682-2000 |
| Mechanical property |
Rating |
Test method |
| Tensile strength |
59.21MPa |
GB/T 1040-1992 |
| Elongation at break |
123.67/v50% |
GB/T 1040-1992 |
| Flexural strength |
68.79 MPa |
GB/T 9341-2000 |
| Flexural modulus |
1.51GPa |
GB/T 9341-2000 |
| Impact property |
Rating |
Test method |
| Charpy Notched Impact Strength |
29.51KJ/m2 |
GB/T 1043-1993 |
| Charpy impact strength |
25JNBKJ/m2 |
GB/T 1043-1993 |
| Other property |
Rating |
Test method |
| Relative viscosity deviation |
<0.02WT% |
| Relative viscosity |
2.75 |
| Viscosity |
2.81 |
GB/T 1632-1993 |
| Water content |
0.06WT% |
| Tio2content |
0-1.3WT% |
NOTE ISO 9001 2000 |