PC Raw Material with Best Quality

• CAS No.: (67-07-2)_
• Formula: -[CH2-CH2]N-
• EINECS: 231-159-6
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Model NO.: PC 1070
• Plastic Forming Method: Injection
• Color: Transparency
• Mfr: 10 G/10min
• Payment: T/T L/C
• Delivery: Within 10 Days After Receiving Deposit
• Transport Package: 25kg/Bag
• Specification: SGS
• Origin: China
• HS Code: 3904109090
• Production Capacity: 200t/Month

Product Description

Recycled & Virgin

1. Description: Homopolymer; Injection grade

2. Appearance: Clear/transparency

3. Applications: Optic lighting; Electronic appliances; Mechanical equipment

Optic lighting: Used in the manufacture of large chimney, protective glass also can be used in transparent Material on the plane.
Electronic appliances: CD, telephones, computers, videos and so on.
Mechanical equipment: Used in the manufacture of all kinds of parts also can be used to make machine Shell and frame.
Others: Toys, model and so on.

Property item	Test condition	Test method	Test data	Data unit
Density		AS TM D792	1.20
Water absorption		ASTM D570	0.20	%
MFR	300°C 1.2kg	ASTM D1238	10	g/10min
Molding shrinkage		ASTM D955	0.5-0.7	%
Tensile strength		ASTM D638	630	kgf/cm2
Flexural strength	2.8mm/min	ASTM D790	920	kgf/cm2
Flexural modulus	2.8mm/min	ASTM D790	24000	kgf/cm2
IZOD impact strength	1/8	ASTM D256	87	kgf/cm2
Reckwell hardness		ASTM D785	77	M
Distortion temperature	0.45Mpa	ASTM D648	138	°C
Distortion temperature	1.8Mpa	ASTM D648	125	°C
Vicat softening point		ASTM D1525	150	°C
Fire resistance		UL94	V-2

Property item	Test condition	Test method	Test data	Data unit
Density		AS TM D792	1.20
Water absorption		ASTM D570	0.20	%
MFR	300°C 1.2kg	ASTM D1238	10	g/10min
Molding shrinkage		ASTM D955	0.5-0.7	%
Tensile strength		ASTM D638	630	kgf/cm2
Flexural strength	2.8mm/min	ASTM D790	920	kgf/cm2
Flexural modulus	2.8mm/min	ASTM D790	24000	kgf/cm2
IZOD impact strength	1/8	ASTM D256	87	kgf/cm2
Reckwell hardness		ASTM D785	77	M
Distortion temperature	0.45Mpa	ASTM D648	138	°C
Distortion temperature	1.8Mpa	ASTM D648	125	°C
Vicat softening point		ASTM D1525	150	°C
Fire resistance		UL94	V-2