Grade:Film grade, Injection Molding Grade. Impact Copolymer, Random Copolymer, Homopolymer, Fiber Grade and so on.
PACKING: 25KG/BAG
Item |
Test method |
Test data |
Data unit |
Density |
ASTM D-792 |
0.905 |
g/cm3 |
MFR |
ASTM D-1238 |
3.5 |
g/10min |
Tensile yield strength |
ASTM D-638 |
23 |
Mpa |
The yield tensile elongation |
ASTM D-638 |
10 |
% |
Rockwell hardness |
ASTM D-785 |
80 |
% |
notched izod impact strength |
-20ºC |
ASTM D-256 |
100 |
J |
23ºC |
ASTM D-256 |
750 |
J/m |
Flexural modulus |
ASTM D-790A |
1000 |
Mpa |
HDT |
ASTM D-648 |
85 |
ºC |
Vicat Softening Temperature |
ASTM D-1525B |
145 |
ºC |
Data sheet
Performance |
Test conditions [state] |
Test data |
Data unit |
Density |
|
0.9 |
g/m3 |
Melt flow rate |
|
10 |
g/10min |
Tensile yield strength |
|
25 |
Mpa |
Elongation at break |
|
≥600 |
% |
Notch impact strength |
23ºC |
8 |
kJ/ |
Flexural modulus |
|
≥1000 |
Mpa |
Rockwell hardness |
|
90 |
R |
Load heat distortion temperature |
|
80 |
ºC |
APPLICATIONS
The products are widely used and can be used for production of transparency and heat resistance have higher requirements of products, suitable for injection molding, wire drawing, blow molding.
Specification level
Yarn grade
Data sheet
Project |
Quality index |
Test method |
Density,kg/m3 |
0.90-0.905 |
|
MFR,g/10min |
3.2 |
GB/T 3682-2000 |
Tensile Yield Strength,MPa ≥ |
35.2 |
ASTM D-638 |
Isotactic index %(m/m) ≥ |
98.4 |
GB/T 2412-80 |
Cleanliness,corlor, per/kg |
11-20 |
SH/T 1541-93 |
Powder ash % ≤ |
0.017 |
GB/T 9345-88 |
APPLICATIONS
Used for woven bag